Abstract:The use of additive manufacturing technologies to produce lightweight or functional structures is widespread. Especially Ti 6 Al 4 V plays an important role in this development field and parts are manufactured and analyzed with the aim to characterize the mechanical properties of open-porous structures and to generate scaffolds with properties specific to their intended application. An SLM and an EBM process were used respectively to fabricate the Ti 6 Al 4 V single struts. For mechanical characterization, uniaxial compression tests and hardness measurements were conducted. Furthermore, the struts were manufactured in different orientations for the determination of the mechanical properties. Roughness measurements and a microscopic characterization of the struts were also carried out. Some parts were characterized following heat treatment (hot isostatic pressing). A functional correlation was found between the compressive strength and the slenderness ratio (λ) as well as the equivalent diameter (d) and the height (L) of EBM and SLM parts. Hardness investigations revealed considerable differences related to the microstructure. An influence of heat treatment as well as of orientation could be determined. In this work, we demonstrate the influence of the fabrication quality of single struts, the roughness and the microstructure on mechanical properties as a function of orientation.

The propensity to manufacture functional and geometrically sophisticated parts from a wide range of metals provides the metal additive manufacturing (AM) processes superior advantages over traditional methods. The field of metal AM is currently dominated by beam-based technologies such as selective laser sintering (SLM) or electron beam melting (EBM) which have some limitations such as high production cost, residual stress and anisotropic mechanical properties induced by melting of metal powders followed by rapid solidification. So, there exist a significant gap between industrial production requirements and the qualities offered by well-established beam-based AM technologies. Therefore, beamless metal AM techniques (known as non-beam metal AM) have gained increasing attention in recent years as they have been found to be able to fill the gap and bring new possibilities. There exist a number of beamless processes with distinctively various characteristics that are either under development or already available on the market. Since this is a very promising field and there is currently no high-quality review on this topic yet, this paper aims to review the key beamless processes and their latest developments.

No abstract

3D printing is a promising method for the fabrication of scaffolds in the field of bone tissue engineering. To date, the mechanical strength of 3D printed ceramic scaffolds is not sufficient for a variety of applications in the reconstructive surgery. Mechanical strength is directly in relation with the porosity of the 3D printed scaffolds. The porosity is directly influenced by particle size and particle-size distribution of the raw material. To investigate this impact, a hydroxyapatite granule blend with a wide particle size distribution was fractioned by sieving. The specific fractions and bimodal mixtures of the sieved granule blend were used to 3D print specimens. It has been shown that an optimized arrangement of fractions with large and small particles can provide 3D printed specimens with good mechanical strength due to a higher packing density. An increase of mechanical strength can possibly expand the application area of 3D printed hydroxyapatite scaffolds.

No abstract