TiO/g-CN photocatalysts with the ratio of TiO to g-CN ranging from 0.3/1 to 2/1 were prepared by simple mechanical mixing of pure g-CN and commercial TiO Evonik P25. All the nanocomposites were characterized by X-ray powder diffraction, UV-vis diffuse reflectance spectroscopy, photoluminescence, X-ray photoelectron spectroscopy, Raman spectroscopy, infrared spectroscopy, transmission electron microscopy, photoelectrochemical measurements, and nitrogen physisorption. The prepared mixtures along with pure TiO and g-CN were tested for the photocatalytic reduction of carbon dioxide and photocatalytic decomposition of nitrous oxide. The pure g-CN exhibited the lowest photocatalytic activity in both cases, pointing to a very high recombination rate of charge carriers. On the other hand, the most active photocatalyst toward all the products was (0.3/1)TiO/g-CN. The highest activity is achieved by combination of a number of factors: (i) specific surface area, (ii) adsorption edge energy, (iii) crystallite size, and (iv) efficient separation of the charge carriers, where the efficient charge separation is the most decisive parameter.

No abstract

No abstract

No abstract

In this paper, a sol-gel derived mesoporous polymeric carbon nitride has been investigated as a photocatalyst for CO2 photocatalytic reduction. Noble-metal Pt nanoparticles were deposited on carbon nitride (sg-CN) in order to investigate the performance of both Pt-sg-CN and sg-CN for photocatalytic CO2 reduction. Physicochemical properties of prepared nanocomposites were comprehensively characterized by using powder XRD, N2 physisorption, UV-Vis DRS, ICP-AES, FTIR, solid-state NMR, SEM, TEM and photoelectrochemical measurements. Compared with pure sg-CN, the resulting Pt-loaded sg-CN (Pt-sg-CN) exhibited significant improvement on the CO2 photocatalytic reduction to CH4 in the presence of water vapor at ambient condition under UV irradiation. 1.5 wt.% Pt-loaded sg-CN (Pt-sg-CN) photocatalyst formed the highest methane yield of 13.9 μmol/gcat. after 18 h of light irradiation, which was almost 2 times and 32 times improvement in comparison to pure sg-CN and commercial TiO2 Evonik P25, respectively. The substantial photocatalytic activity of Pt-sg-CN photocatalyst for the yield product of the CO2 photocatalytic reduction was attributed to the efficient interfacial transfer of photogenerated electrons from sg-CN to Pt due to the lower Fermi level of Pt in the Pt-sg-CN hybrid heterojunctions as also evidenced by photo-electrochemical measurements. This resulted in the reduction of electron-hole pairs recombination for effective spatial charge separation, consequently increasing the photocatalytic efficiency.