A hexagonal packing of rod like structures is proposed in solutions and gels of a perfluorinated ionomer. The diameter of the rods has been obtained by two different approaches either geometrical from shifts of the interference peak versus concentrations in small angle scattering experiments or direct from analysis of the structure factor in diluted solutions. Consistent results give values between 18 and 31 Å for the radius of the rods, depending on the solvent. The rods have a perfluorinated core with the charges on the surface and the diameter depends on the surface tension rather than on the dielectric constant of the solvent. The structure may result from a balance between elastic and interfacial energies as it is shown by calculations

No abstract

Deuterium oxide solutions of schizophyllan, a triple-helical polysaccharide, undergoing an order-disorder transition centered at 17 degrees C, were studied by optical rotation (OR) and heat capacity (C(p)) to elucidate the molecular mechanism of the transition and water structure in the solution and frozen states. The ordered structure at low temperature consisted of the side chains and water in the vicinity forming an ordered hydrogen-bonded network surrounding the helix core and was disordered at higher temperature. In the solution state appeared clearly defined transition curves in both the OR and C(p) data. The results for three samples of different molecular weights were analyzed theoretically, treating this transition as a typical linear cooperative transition from the ordered to disordered states and explained quantitatively if the molecular weight polydispersity of the sample was considered. The excess heat capacity C(EX)(p) defined as the C(p) minus the contributions from schizophyllan and D(2)O was estimated. In the frozen state it increased with raising temperature above 150 K until the mixture melted. This was compared with the dielectric increment observed in this temperature range and ascribed to unfreezable water. From the heat capacity and dielectric data, unfreezable water is mobile but more ordered than free water. In the solution state, the excess heat capacity originates from the interactions of D(2)O molecules as bound water and structured water, and so forth. Thus the schizophyllan triple helix molds water into various structures of differing orders in solution and in the solid state.

Deuterium oxide solutions of a triple-helical polysaccharide schizophyllan, undergoing an order-disorder transition centered around 17 degrees C, were studied by the time-domain reflectometry (TDR) to obtain dielectric dispersions in the solution and frozen states. In the solution state, the dispersion below the transition temperature is resolved in three dispersions (relaxation times at 0 degrees C) ascribed to side chain glucose residue (1; 102 ns), structured water (s; 2.0 ns) and bulk water (h), respectively, from low to high frequencies. Bulk water is divided into slow water (h2; 0.04 ns) and free or pure water (h1; 0.02 ns). Above the transition temperature structured water almost disappears and is compensated by slow water. Structured water is similar to bound water for proteins but different from it because of this transition behavior. Another dispersion (l) seen at the lowest frequency is assigned to the rotation of side-chain glucose residue coupled with hydrated water. Parts of this dispersion and structured water are suggested to constitute bound water. In the frozen state were observed a major dispersion (h; 0.14 ns) and a minor one (m; 28 ns), which were ascribed to considerably mobile and less mobile waters. They are similar to but not exactly the same as that for unfreezable water in bovine serum albumin solutions argued by Miura et al. (Biopolymers, 1995, Vol. 36, p. 9). Water is molded into different structures by the triple helix.