Friction stir welding was applied to a 2 mm thick 304 austenitic stainless steel plate. The microstructural evolution and hardness distribution in the weld were investigated. The stir zone (SZ) and thermomechanically affected zone (TMAZ) showed dynamically recrystallised and recovered microstructures, respectively, which are typically observed in friction stir welds in aluminium alloys. The hardness of the SZ was higher than that of the base material and the maximum hardness was observed at the TMAZ. The higher hardness at the TMAZ was attributed to high densities of dislocations and subboundaries. Microstructural observations revealed that the ferrite was formed along grain boundaries of the austenite matrix in the advancing side of the SZ. It is suggested that the frictional heat due to stirring resulted in the phase transformation of austenite to ferrite and that upon rapid cooling the ferrite was retained in the SZ.
The wear of polycrystalline cubic boron nitride (pcBN) tool and its effect on second phase formation were investigated in stainless steel friction-stir (FS) welds. The nitrogen content and the flow stress were analyzed in these welds to examine pcBN tool wear. The nitrogen content in stir zone (SZ) was found to be higher in the austenitic stainless steel FS welds than in the ferritic and duplex stainless steel welds. The flow stress of austenitic stainless steels was almost 1.5 times larger than that of ferritic and duplex stainless steels. These results suggest that the higher flow stress causes the severe tool wear in austenitic stainless steels, which results in greater nitrogen pickup in austenitic stainless steel FS welds. From the microstructural observation, a possibility was suggested that Cr-rich borides with a crystallographic structure of Cr 2 B and Cr 5 B 3 formed through the reaction between the increased boron and nitrogen and the matrix during FS welding (FSW).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.