A study of the structure-composition-properties correlation is reported for the oxygen-deficient SrFeCoO (x = 0.1-0.85) materials. The introduction of Co in the parent SrFeO (SrFeO) structure revealed an interesting structural transformation. At room temperature (RT), an orthorhombic (space group Cmmm, 2√2a × 2a × √2a type, a = lattice parameter of the cubic perovskite) → tetragonal (space group P4/mmm, a × a × 2a type) → tetragonal (space group I4/mmm, 2a × 2a × 4a type) structural transformation is observed in parallel with increasing Co content and decreasing oxygen content in the structure. At the same time, a rich variation in the magnetic properties is explored. The samples with x = 0.25, 0.3 show temperature-induced magnetization reversal. With increasing Co content in the structure, magnetic interactions start to weaken due to the random distribution of Fe and Co in the structure; the x = 0.5 sample shows frustration in the magnetic behavior with much smaller magnetization value. With a further increase in the Co content in the structure, RT ferrimagnetic-type behavior is observed for the sample with x = 0.85. The nuclear and magnetic structure refinements using RT and low-temperature neutron powder diffraction (NPD, 10 K) patterns confirm the formation of a "314-type" novel oxygen vacancy ordered phase for the sample with x = 0.85, which is the first case of "314-type" novel oxygen vacancy ordering without A-site (ABO type perovskite) ordering. The magnetic structure is G-type antiferromagnetic starting at room temperature. Further, the stabilization of the "314-type" complex superstructure is related to the ordering of oxygen vacancies in the oxygen-deficient Co-O layers, and the same assists in building a network of Co ions with different coordination environments, each with different spin states, and forms the spin-state ordering.
HAL is a multidisciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L'archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d'enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.
We describe the synthesis and the crystallographic and magnetic properties of a novel NaCoCr2(PO4)3 phosphate. A conventional solid-state reaction was used to obtain single-phase powders. A Rietveld analysis of powder X-ray diffraction data proposes an orthorhombic symmetry similar to α-CrPO4-type structure in space group Imma with the following unit cell parameters: a = 10.413(1) Å; b = 13.027(1) Å; c = 6.372(1) Å. The framework consists of PO4 tetrahedra, M(1)O6 (M(1) = Cr) octahedra, and M(2)2O10 (M(2) = 0.5Cr+0.5Co) binuclear unit of edge-sharing MO6 octahedra. It can be described in terms of two building blocks: sheets consisting of corner-sharing M(2)2O10 units with PO4 tetrahedra found parallel to the (b,c) plane, and chains made by corner-sharing CrO6 octahedra and PO4 tetrahedra running along the b axis. From the interconnection of the sheets and chains, a 3D rigid skeleton is formed, exhibiting two kinds of intersecting tunnel channels containing the Na(+) ions. The proposed structure derives from the α-CrPO4-type structure considering a positive charge balance according to the equation Cr(3+) → Co(2+) + Na(+), resulting in sodium countercation introduction within the unoccupied channels shown in the α-CrPO4 framework. Temperature-dependent DC and AC magnetic susceptibility is indicative of a long-range magnetic ordering occurring at 32 K. Further, spin-flop transition sheds light on a chromium-based phosphate for the first time.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.