This article describes the room-temperature fracture behavior of ductile-phase-toughened V-V 3 Si in situ composites that were produced by arc melting (AM), cold-crucible induction melting (IM), and cold-crucible directional solidification (DS). Composites were produced containing a wide range of microstructures, interstitial impurity contents, and volume fractions of the ductile V-Si solid solution phase, denoted (V). The fracture toughness of these composites generally increases as the volume fraction of (V) increases, but is strongly influenced by the microstructure, the mechanical properties of the component phases, and the crystallographic orientation of the (V) phase with respect to the maximum principal stress direction. For eutectic composites that have a (V) volume fraction of about 50 pct, the fracture toughness increases with decreasing ''effective'' interstitial impurity concentration, [I] ϭ [N] ϩ 1.33 [O] ϩ 9 [H]. As [I] decreases from 1400 ppm (AM) to 400 ppm (IM), the fracture toughness of the eutectic composites increases from 10 to 20 MPa. Further, the fracture ͌m toughness of the DS eutectic composites is greater when the crack propagation direction is perpendicular, rather than parallel, to the composite growth direction. These results are discussed in light of conventional ductile-phase bridging theories, which alone cannot fully explain the fracture toughness of V-Si in situ composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.