Bulk nanostructured perovskites of La 0.67-x Li 3x TiO 3 (LLTO) were prepared by using thermally ball-grinding from compounds of La 2 O 3 , Li 2 CO 3 and TiO 2 . From XRD analysis, it was found that LTTO materials were crystallized with nano-size grains of an average size of 30 nm. The bulk ionic conductivity was found strongly dependent on the Li + composition, the samples with x = 0.11 (corresponding to a La 0.56 Li 0.33 TiO 3 compound) have the best ionic conductivity, which is ca. 3.2 x 10 -3 S/cm at room temperature. The LLTO amorphous films were made by electron beam deposition. At room temperature the smooth films have ionic conductivity of 3.5 x 10 -5 S/cm and transmittance of 80%. The optical bandgap of the films was found to be of 2.3 eV. The results have shown that the perovskite La 0.56 Li 0.33 TiO 3 thin films can be used for a transparent solid electrolyte in ionic battery and in all-solid-state electrochromic devices, in particular.
Crystalline perovskite La0.67-xLi 3x TiO 3 with x = 0.06, 0.11 and 0.15 were prepared by solid-state-solution reactions at 1350 0 C from TiO 2 , La 2 O 3 and Li 2 CO 3 Crystalline structure of these compounds was analyzed by XRD method. The ionic conducting property of La 0.67-x Li 3xTiO 3 was characterized on AutoLab. Potentiostat-PGS30 system with impedance technique using fitting software program available in the equipment. The highest ion conductivity at room temperature was found for the compound with x =0.11, namely $\sigma$ = 3.1 x 10 -5Scm -1. With increase of temperature the ionic conductivity increased and at 2000C it reached a value in two orders in magnitude higher (6 x 10 -3Scm -1). The activation energy of the compounds was determined on Ln($\sigma$) vs. 1/T plots and found to be as low as 0.36 eV.
With the aim of producing all-solid-state electrochromic mirrors, La 0.67−x Li 3x TiO 3 (LLTO) and the WO 3 were prepared by electron beam deposition. The LLTO (with x = 0.11) powder was synthesized by thermally ball-grinding method and the Li + ionic conductivity of the LLTO ceramic targets was found to be of ca. 3.25 × 10 −3 S/cm. Using LLTO targets for e-beam evaporation, 300 nm-thick films with the Li + ionic conductivity of 5.50 × 10 −5 S/cm were deposited. Combining LLTO films with WO 3 /ITO and LiMn 2 O 4 layers, all-solid-state electrochromic mirrors with a laminar structure of Al/LiMn 2 O 4 /LLTO/WO 3 /ITO were prepared. The reversible reflectance of the mirrors was well controlled by applying polarized potentials onto the ITO electrode. The obtained results suggest useful applications for electrochromic windows working as a smart reflectance mirror that can be used for auto rear-view mirrors.
Perovskite La\(_{(2/3) - x}\)Li\(_{3x}\)TiO\(_{3}\) samples with 0.06 \( \leq x \leq 0.15\) were prepared by a double mechanical alloying method. Structure and Li$^{ + }$-ion conductive properties of the La\(_{(2 / 3) - x}\)Li\(_{3x}\)TiO\(_{3}\) samples were investigated. Most of the analyzed perovskite samples exhibit a double unit cell. In these samples, a change of symmetry from tetragonal to orthorhombic is observed for sample with lithium content x = 0.06. Structural modifications were obtained mainly due to the cation vacancies ordering along the c-axis, which disappeared gradually when the lithium content increased. At room temperature, the maximum values of grains and grain boundaries conductivities of the La\(_{(2 / 3) - x}\)Li\(_{3x}\)TiO\(_{3}\) samples were found to be of \(1.5\times 10$^{ - 3}\) S/cm and \(5.8 \times 10^{ - 5}\) S/cm, respectively. The temperature dependence of ionic conductivity obeyed a non-Arrhenius behaviour. At temperature from 30 to 125\(^{\circ}\)C, the activation energy for grain and grain-boundary conductivity was found to be of $\sim $ 0.23 eV and $\sim $ 0.32 eV, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.