In this paper, we report the optoelectronic properties of multi-layered GeS nanosheet (∼28 nm thick)-based field-effect transistors (called GeS-FETs). The multi-layered GeS-FETs exhibit remarkably high photoresponsivity of Rλ ∼ 206 A W(-1) under 1.5 μW cm(-2) illumination at λ = 633 nm, Vg = 0 V, and Vds = 10 V. The obtained Rλ ∼ 206 A W(-1) is excellent as compared with a GeS nanoribbon-based and the other family members of group IV-VI-based photodetectors in the layered-materials realm, such as GeSe and SnS2. The gate-dependent photoresponsivity of GeS-FETs was further measured to be able to reach Rλ ∼ 655 A W(-1) operated at Vg = -80 V. Moreover, the multi-layered GeS photodetector holds high external quantum efficiency (EQE ∼ 4.0 × 10(4)%) and specific detectivity (D* ∼ 2.35 × 10(13) Jones). The measured D* is comparable to those of the advanced commercial Si- and InGaAs-based photodiodes. The GeS photodetector also shows an excellent long-term photoswitching stability over a long period of operation (>1 h). These extraordinary properties of high photocurrent generation, broad spectral range, and long-term stability make the GeS-FET photodetector a highly qualified candidate for future optoelectronic applications.

Molybdenum disulfide (MoS2) is a promising catalyst for hydrogen evolution reaction (HER) because of its unique nature to supply active sites in the reaction. However, the low density of active sites and their poor electrical conductivity have limited the performance of MoS2 in HER. In this work, we synthesized MoS2 nanosheets on three-dimensional (3D) conductive MoO2 via a two-step chemical vapor deposition (CVD) reaction. The 3D MoO2 structure can create structural disorders in MoS2 nanosheets (referred to as 3D MoS2/MoO2), which are responsible for providing the superior HER activity by exposing tremendous active sites of terminal disulfur of S2(-2) (in MoS2) as well as the backbone conductive oxide layer (of MoO2) to facilitate an interfacial charge transport for the proton reduction. In addition, the MoS2 nanosheets could protect the inner MoO2 core from the acidic electrolyte in the HER. The high activity of the as-synthesized 3D MoS2/MoO2 hybrid material in HER is attributed to the small onset overpotential of 142 mV, a largest cathodic current density of 85 mA cm(-2), a low Tafel slope of 35.6 mV dec(-1), and robust electrochemical durability.