Fully printed perovskite solar cells are demonstrated with slot-die coating, a scalable printing method. A sequential slot-die coating process is developed to produce efficient perovskite solar cells and to be used in a large-scale roll-to-roll printing process. All layers excluding the electrodes are printed and devices demonstrate up to 11.96% power conversion efficiency. It is also demonstrated that the new process can be used in roll-to-roll production.
Solution-processed organic photovoltaic cells (OPVs) hold great promise to enable roll-to-roll printing of environmentally friendly, mechanically flexible and cost-effective photovoltaic devices. Nevertheless, many high-performing systems show best power conversion efficiencies (PCEs) with a thin active layer (thickness is ~100 nm) that is difficult to translate to roll-to-roll processing with high reproducibility. Here we report a new molecular donor, benzodithiophene terthiophene rhodanine (BTR), which exhibits good processability, nematic liquid crystalline behaviour and excellent optoelectronic properties. A maximum PCE of 9.3% is achieved under AM 1.5G solar irradiation, with fill factor reaching 77%, rarely achieved in solution-processed OPVs. Particularly promising is the fact that BTR-based devices with active layer thicknesses up to 400 nm can still afford high fill factor of ~70% and high PCE of ~8%. Together, the results suggest, with better device architectures for longer device lifetime, BTR is an ideal candidate for mass production of OPVs.
We report the synthesis and bulk heterojunction photovoltaic performance of the first dithienogermole (DTG)-containing conjugated polymer. Stille polycondensation of a distannyl-DTG derivative with 1,3-dibromo-N-octyl-thienopyrrolodione (TPD) results in an alternating copolymer which displays light absorption extending to 735 nm, and a higher HOMO level than the analogous copolymer containing the commonly utilized dithienosilole (DTS) heterocycle. When polyDTG-TPD:PC(70)BM blends are utilized in inverted bulk heterojunction solar cells, the cells display average power conversion efficiencies of 7.3%, compared to 6.6% for the DTS-containing cells prepared in parallel under identical conditions. The performance enhancement is a result of a higher short-circuit current and fill factor in the DTG-containing cells, which comes at the cost of a slightly lower open circuit voltage than for the DTS-based cells.
Interface recombination induced by the defect states in zinc‐oxide‐nanoparticle‐based electron extraction layer is reported as a significant loss‐mechanism of photocurrent collection. By choosing appropriate UV–ozone treatment conditions on the zinc oxide layer, inverted polymer solar cells show reduced interface recombination and thus improved power conversion efficiencies of up to 8.1%.
The evolution of electronic energy levels of controlled air and oxygen exposed molybdenum trioxide (MoO3) films has been investigated with ultraviolet photoemission spectroscopy, inverse photoemission spectroscopy, and x-ray photoemission spectroscopy. We found that while most of the electronic levels of as deposited MoO3 films remained largely intact, the reduction in the work function (WF) was substantial. The gradual surface WF change from 6.8 to 5.3 eV was observed for air exposed film, while oxygen exposed film the surface WF saturated at ∼5.7 eV. Two distinct stages of exposure are observed, the first dominated by oxygen adsorption for <1013 Langmuir (L) exposure and at the final step moisture absorption >1013 L.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.