No abstract

Salt damage can affect the service life of numerous building structures, both historical and contemporary, in a significant way. In this review, various damage mechanisms to porous building materials induced by salt action are analyzed. The importance of pretreatment investigations is discussed as well; in combination with the knowledge of salt and moisture transport mechanisms they can give useful indications regarding treatment options. The methods of salt damage treatment are assessed then, including both passive techniques based on environmental control, reduction of water transport, or conversion to less soluble salts and active procedures resulting in the removal of salts from deterioration zones. It is concluded that cellulose can still be considered as the favorite material presently used in desalination poultices but hydrophilic mineral wool can serve as its prospective alternative in future applications. Another important cause of building pathologies is the rising damp and, in this phenomenon, it is particularly severe considering the presence of salts in water. The treatment of rising damp in historic building walls is a very complex procedure and at Laboratory of Building Physics (LFC-FEUP) a wall base hygroregulated ventilation system was developed and patented.

In many European countries, energy poverty is measured on the basis of real energy bills, as theoretical energy costs are hard to calculate. The UK is an exception—the data inputs for the Low Income-High Cost (LIHC) indicator are based on reasonable energy costs, these data are collected through specially designed surveys, often an intensive and costly procedure. Approaches which calculate energy needs are valid when energy bill data are unreliable or where households restrict consumption. In this analysis, energy poverty levels are evaluated for Greece, the municipality of Évora (Portugal), and the Basque Country (Spain): energy bills are modeled based on building energy performance data and other energy uses, and adjusted according to socio-demographic variables. To this end, equivalization weights are calculated using socio-economic data from the aforementioned southern European countries/regions. Data are analyzed to compare measurements with actual versus modeled bills using the Ten-Percent Rule (TPR) and Hidden Energy Poverty (HEP) against twice the median (2M) indicator, enhancing the identification of households with low energy consumption. In conclusion, theoretical energy needs can be combined with socio-demographic data instead of actual energy bills to measure energy poverty in a simplified way, avoiding the problem of targeting households that under consume.

The stability of tubular metal supported SOFC has been studied as a function of current load, thermal cycles and interconnect-sealing concepts. Long term testing under applied current at 800ºC have been performed over 1000 hours on standard cells. Thermal cycles have been proven intensely (250 cycles) during over 700 hours. Major cause for degradation has been identified in terms of the anode interconnect-sealing design, which involves specific handling and machining of tubes and generation of initial submicron cracks. Cell microstructure seems stable after 1000 hours testing at 300 mA/cm2 and 800ºC.