Unique spindle-shaped nanoporous anatase TiO(2) mesocrystals with a single-crystal-like structure and tunable sizes were successfully fabricated on a large scale through mesoscale assembly in the tetrabutyl titanate-acetic acid system without any additives under solvothermal conditions. A complex mesoscale assembly process involving slow release of soluble species from metastable solid precursors for the continuous formation of nascent anatase nanocrystals, oriented aggregation of tiny anatase nanocrystals, and entrapment of in situ produced butyl acetate as a porogen was put forward for the formation of the anatase mesocrystals. It was revealed that the acetic acid molecules played multiple key roles during the nonhydrolytic processing of the [001]-oriented, single-crystal-like anatase mesocrystals. The obtained nanoporous anatase mesocrystals exhibited remarkable crystalline-phase stability (i.e., the pure phase of anatase can be retained after being annealed at 900 °C) and improved performance as anode materials for lithium ion batteries, which could be largely attributed to the intrinsic single-crystal-like nature as well as high porosity of the nanoporous mesocrystals.
Owing to the layered structure and high theoretical capacity, MoS2 has attracted more and more interest as a potential anode material for lithium-ion batteries. However, it suffers from rapid capacity decay and low rate capability. In this work, we introduce a novel hierarchical material consisting of ultrathin MoS2 nanosheets grown on the surface of an active carbon fiber (ACF) cloth fabricated by a facile morphogenetic process. The ACF cloth acts as both a template and a stabilizer. The obtained MoS2/ACF cloth composite possesses hierarchical porosity and an interconnected framework. Serving as a free-standing and binder-free anode, it shows high specific capacity and excellent reversibility. A discharge capacity as high as 971 mA h g(-1) is attained at a current density of 0.1 A g(-1), and the capacity fade is only 0.15% per cycle within 90 cycles. Even after 200 cycles at a high current density of 0.5 A g(-1), the composite still shows a capacity of 418 mA h g(-1). The superior electrochemical performance of MoS2/ACF can be attributed to its robust structure and to the synergistic effects of ultrathin MoS2 nanosheets and ACF. This single-component anode that we propose benefits from a simplified electrode preparation process. The morphogenetic strategy used for the material production is facile but effective, and can be extended to prepare other metal sulfides with elaborate textural characteristics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.