Using a 820 nm-thick high-quality Ge0.97Sn0.03 alloy film grown on Si(001) by molecular beam epitaxy, GeSn p-i-n photodectectors have been fabricated. The detectors have relatively high responsivities, such as 0.52 A/W, 0.23 A/W, and 0.12 A/W at 1310 nm, 1540 nm, and 1640 nm, respectively, under a 1 V reverse bias. With a broad detection spectrum (800-1800 nm) covering the whole telecommunication windows and compatibility with conventional complementary metal-oxide-semiconductors (CMOS) technology, the GeSn devices are attractive for applications in both optical communications and optical interconnects.

No abstract

Surface-illuminated GeSn p-i-n photodetectors (PDs) with Ge0.964Sn0.036 active layer on Ge substrate were fabricated. Photodetection up to 1.95 μm is achieved with a responsivity of 0.13 A/W. High responsivities of 0.56 and 0.71 A/W were achieved under a reverse bias voltage of 3 V at 1640 and 1790 nm, respectively. A low dark current of 1.08 μA was obtained at a reverse bias of 1 V with a diameter of 150 μm, which corresponds to a current density of 6.1 mA/cm2. This value is among the lowest dark current densities reported among GeSn PDs.