The new double perovskite Mn2MnReO6 has been synthesised at high pressure. Mn(2+) and Re(6+) spins order antiferromagnetically through two successive transitions that are coupled by magnetoelastic effects, as order of the Mn spins at 109 K leads to lattice distortions that reduce frustration prompting Re order at 99 K.
EuPtAl has been prepared from the elements via arc-melting and subsequent temperature treatment; the structure was refined from single crystal X-ray diffraction data. The compound crystallizes in an orthorhombic (3 + 1)D commensurately modulated structure (ScPtAl type) with space group Cmcm(α,0,0)0 s0 (α = 2/3). Full ordering of the Pt and Al atoms within the [PtAl] polyanion was observed. Magnetic measurements revealed an anomaly in the susceptibility data at T = 41.6(1) K, which was also observed as λ-type anomaly in heat capacity measurements ( T = 40.7(1) K). Temperature dependent powder X-ray diffraction experiments indicated a drastic shortening of the c axis (-18 pm, -1.1%) around 45 K, while the a axis nearly remains the same (-1 pm, -0.2%). Measurements of the electrical resistivity verified the anomaly, indicating a clear change in the electronic structure of the material. The observed anomalies in the physical measurements can be explained by a temperature driven first order valence change from Eu at higher temperatures (>55 K) to Eu at low temperatures. This valence change was proven by temperature dependent Eu Mössbauer spectroscopic investigations. Isostructural EuPtGa was prepared in comparison, and it shows divalent Eu atoms down to 2.5 K along with antiferromagnetic ordering at T = 13.1(1) K.
Ba3Pt4Al4 was prepared from the elements in niobium ampules and crystallizes in an orthorhombic structure, space group Cmcm (oP44, a = 1073.07(3), b = 812.30(3), c = 1182.69(3) pm) isopointal to the Zintl phase A2Zn5As4 (A = K, Rb). The structure features strands of distorted [Pt4Al4] heterocubane-like units connected by condensation over Pt/Al edges. These are arranged in a hexagonal rod packing by further condensation over Pt and Al atoms with the barium atoms located inside cavities of the [Pt4Al4](δ-) framework. Structural relaxation confirmed the electronic stability of the new phase, while band structure calculations indicate metallic behavior. Crystal orbital Hamilton bonding analysis coupled with Bader effective charge analysis suggest a polar intermetallic phase in which strong Al-Pt covalent bonds are present, while a significant electron transfer from Ba to the [Pt4Al4](δ-) network is found. By X-ray photoelectron spectroscopy measurements the Pt 4f5/2 and 4f7/2 energies for Ba3Pt4Al4 were found in the range of those of elemental Pt due to the electron transfer of Ba, while PtAl and PtAl2 show a pronounced shift toward a more cationic platinum state. (27)Al magic-angle spinning NMR investigations verified the two independent crystallographic Al sites with differently distorted tetrahedrally coordinated [AlPt4] units. Peak assignments could be made based on both geometrical considerations and in relation to electric field gradient calculations.
Structural and property investigations of the five Zintl phases Eu5In2Pn6 and Eu3MAs3 (Pn = As–Bi; M = Al, Ga) including magnetic and 121Sb and 151Eu Mössbauer spectroscopic measurements.
REPd5Al2 compounds with RE = Ce–Gd as well as Y and Lu have been previously synthesized. Although some compounds with the small lanthanides also exist, the compounds with intermediate-sized rare-earth elements (RE = Tb–Yb) had not been prepared. We report on the missing members of the REPd5Al2 (RE = Tb–Yb) series as well as on the new REPt5Al2 (RE = Y, Gd–Tm, Lu) series, which we have synthesized and structurally as well as magnetically characterized. All members crystallize isostructurally in the ZrNi2Al5 type with an anti-arrangement of the T = Pd/Pt and Al atoms. YPd5Al2 and LuPd5Al2, as well as the respective platinum homologs, YPt5Al2 and LuPt5Al2, have been characterized also by 27Al magic-angle spinning nuclear magnetic resonance spectroscopy. Consistent with the XRD analysis, the spectra indicate the existence of only one distinct Al site in the structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.