Abstract:The magnetic phase diagrams of RMnO 3 (R = Er, Yb, Tm, Ho) are investigated up to 14 Tesla via magnetic and dielectric measurements. The stability range of the AFM order below the Néel temperature of the studied RMnO 3 extends to far higher magnetic fields than previously assumed. Magnetic irreversibility indicating the presence of a spontaneous magnetic moment is found near 50 K for R=Er, Yb, and Tm. At very low temperatures and low magnetic fields the phase boundary defined by the ordering of the rare earth moments is resolved. The sizable dielectric anomalies observed along all phase boundaries are evidence for strong spin-lattice coupling in the hexagonal RMnO 3 . In HoMnO 3 the strong magnetoelastic distortions are investigated in more detail via magnetostriction experiments up to 14 Tesla. The results are discussed based on existing data on magnetic symmetries and the interactions between the Mn-spins, the rare earth moments, and the lattice.

REBa2Cu3Ox ((REBCO), RE = rare earth) superconductor tapes with moderate levels of dopants have been optimized for high critical current density in low magnetic fields at 77 K, but they do not exhibit exemplary performance in conditions of interest for practical applications, i.e., temperatures less than 50 K and fields of 2–30 T. Heavy doping of REBCO tapes has been avoided by researchers thus far due to deterioration in properties. Here, we report achievement of critical current densities (Jc) above 20 MA/cm2 at 30 K, 3 T in heavily doped (25 mol. % Zr-added) (Gd,Y)Ba2Cu3Ox superconductor tapes, which is more than three times higher than the Jc typically obtained in moderately doped tapes. Pinning force levels above 1000 GN/m3 have also been attained at 20 K. A composition map of lift factor in Jc (ratio of Jc at 30 K, 3 T to the Jc at 77 K, 0 T) has been developed which reveals the optimum film composition to obtain lift factors above six, which is thrice the typical value. A highly c-axis aligned BaZrO3 (BZO) nanocolumn defect density of nearly 7 × 1011 cm−2 as well as 2–3 nm sized particles rich in Cu and Zr have been found in the high Jc films.

The critical current and structural properties of (Gd,Y)BaCuO tapes made by metal organic chemical vapor deposition (MOCVD) with Zr addition levels up to 30 at.% have been investigated. The reduction in critical current beyond the previously optimized Zr addition level of 7.5 at.% was found to be due to structural deterioration of the (Gd,Y)Ba 2 Cu 3 O x film. By a modified MOCVD process, enhanced critical current densities have been achieved with high levels of Zr addition, including 3.83 MA cm −2 in 15 at.% Zr-added 1.1 µm thick film at 77 K in zero magnetic field. Critical currents as high as 1072 A/12 mm have been reached in (Gd,Y)BaCuO tapes with 15 at.% Zr addition at 30 K in a field of 3 T applied perpendicular to the tape, corresponding to a pinning force value of 268 GN m −3 . The enhanced critical currents achievable with a high density of nanoscale defects by employing high levels of second-phase additions enable the performance targets needed for the use of HTS tapes in coil applications involving high magnetic fields at temperatures below 50 K to be met.

A critical current (I c ) value of 3963 A/12 mm, corresponding to a critical current density (J c ) of 15 MA cm −2 has been achieved at 30 K, 3 T in the orientation of field parallel to the c-axis (B||c) in 2.2 μm thick film (Gd,Y)BaCuO tapes with 20 mol% Zr addition made by metal organic chemical vapor deposition. This J c level is more than a factor of four higher than the J c values of 7.5 mol% Zr-added tapes, which are an industry benchmark. The critical current values in a magnetic field of 3 T parallel to the c-axis in the 2.2 μm thick, 20 mol% Zr-added tape reached 2833 A/12 mm (10.1 MA cm −2 ), 1881 A/12 mm (7.1 MA cm −2 ) and 805 A/12 mm (3.1 MA cm −2 ) at 40 K, 50 K and 65 K respectively. Such high critical current values were possible because of maintaining a strong alignment of BaZrO 3 nanocolumns along the c-axis over the entire film thickness.

Engineering current density over 5 kA mm −2 at 4.2 K, 14 T in thick film REBCO tapes To cite this article: Goran Majkic et al 2018 Supercond. Sci. Technol. 31 10LT01 View the article online for updates and enhancements. Related content Critical current density above 15 MA cm2 at 30 K, 3 T in 2.2 m thick heavily-doped (Gd,Y)Ba2Cu3Ox superconductor tapes V Selvamanickam, M Heydari Gharahcheshmeh, A Xu et al.-Sample and length-dependent variability of 77 and 4.2 K properties in nominally identical RE123 coated conductors L Rossi, X Hu, F Kametani et al.-Requirements to achieve high in-field critical current density at 30 K in heavilydoped (Gd,Y)Ba2Cu3Ox superconductor tapes V Selvamanickam, M Heydari Gharahcheshmeh, A Xu et al.-Recent citations Goran Majkic-Correlation of In-Field Performance of Thick REBCO Films Between 0-14 T and 4.2-77 K Goran Majkic et al-Effect of Deposition Temperature on Microstructure and Critical Current Properties of Zr-Doped GdYBCO Superconducting Tapes Made by MOCVD Ziming Fan et al