Tin dioxide thin films were obtained by centrifuging. Annealing of samples was carried out in a muffle furnace at a temperature of 400 °C for 15 min, 3, 6 and 12 h. The surface resistance of the films was measured by four-force method. The sensitivity to ethanol vapour was determined by experimental setup that allows measurements in the range from room temperature to 300 °C. There is a change in the acidity of the solution with the addition of ammonium fluoride. To take into consideration this change in acidity, three batches of solutions were prepared: one example without additives, another one ‒ with the addition of ammonium fluoride and the last one ‒ with the addition of ammonium hydroxide. Films synthesized from a film-forming solution containing NH4F have less resistance than films obtained from solutions that do not contain ammonium fluoride. This confirms the presence of fluorine ions in the films as additional sources of free charge carriers. It is found that the pH-indicator of the film-forming solution does not affect the surface resistance of the synthesized SnO2 films. Annealing of fluoride doped films leads to an increase in surface resistance by two orders of magnitude, which is associated with the removal of fluorine from the films and the formation of a large number of defects. Further annealing leads to a decrease in surface resistance, which seems to be associated with a decrease in defects. It is shown that the change in the hydrogen index of the film-forming solution leads to the formation of films with a thermally stable sensitivity to ethanol vapour.
In this work the study on the peculiarities of multiparticle production in interactions of asymmetric nuclei to search for unusual features of such interactions, is performed. A research of long-range and shortrange multiparticle correlations in the pseudorapidity distribution of secondary particles on the basis of analysis of individual interactions of nuclei of 197 Au at energy 10.7 AGeV with photoemulsion nuclei, is carried out. Events with long-range multiparticle correlations (LC), short-range multiparticle correlations (SC) and mixed type (MT) in pseudorapidity distribution of secondary particles, are selected by the Hurst method in accordance with Hurst curve behavior. These types have significantly different characteristics. At first, they have different fragmentation parameters. Events of LC type are processes of full destruction of the projectile nucleus, in which multicharge fragments are absent. In events of mixed type several multicharge fragments of projectile nucleus are discovered. Secondly, these two types have significantly different multiplicity distribution. The mean multiplicity of LC type events is significantly more than in mixed type events. On the basis of research of the dependence of multiplicity versus target-nuclei fragments number for events of various types it is revealed, that the most considerable multiparticle correlations are observed in interactions of the mixed type, which correspond to the central collisions of gold nuclei and nuclei of CNO-group, i.e. nuclei with strongly asymmetric volume, nuclear mass, charge, etc. Such events are characterised by full destruction of the target-nucleus and the disintegration of the projectile-nucleus on several multi-charged fragments.
Аннотация. Тонкие пленки оксида олова получали из пятиводного тетрахлорида олова растворением в 97% этаноле. Концентрация ионов олова в пленкообразующей системе была 0,12 моль/л, 0,16 моль/л, 0,2 моль/л. Пленкообразующую систему SnCl 4 /EtOH наносили на поверхность стеклянных подложек модифицированным методом окунания. Сушили на воздухе и затем отжигали при 400 о С. Было нанесено 4 слоя. Обработка водородной плазмой проводилась при давлении 6,5 Па, мощности 20 Ватт, частоте колебаний создаваемых генератором 27,12 МГц0,6%. Обнаружено уменьшение прозрачности,в пределах точности измерений, пленок, полученных из пленкообразующей системы с концентрацией ионов олова 0,12 моль/л и 0,2 моль/л. Прозрачность пленок, полученных из пленкообразующей системы с концентрацией ионов олова 0,16 моль/л уменьшилось на 3%. Сопротивление пленок уменьшилось в 1,5 раз. Рентгеноструктурный анализ показал рост интенсивности дифракционных пиков от плоскостей кристаллитов SnO 2 . Получен важный технический результат: уменьшение сопротивления тонких пленок SnO 2 без значительного уменьшения прозрачности, при использовании пленкообразующей системы с концентрацией ионов олова 0,12 моль/л и 0,2 моль/л после обработки в течение 3 минут в водородной плазме.Ключевые слова: тонкие пленки, диоксид олова SnO 2 , обработка плазмой, водородная плазма, сопротивление пленок, коэффициент пропускания.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.