Abstract:Freeze-thaw damage is a typical distress incurred in road and railway engineering in cold regions. Concrete waterproofing layer is commonly used in high-speed railway tracks to prevent the penetration of surface water, however, it cracks easily under thermal stress, especially in cold regions. Recently solutions have been proposed to increase the waterproofing layer's cracking resistance by using asphalt layers. Nonetheless, the use of emulsified asphalt as well as dense-graded asphalt mixture were not effective enough. To improve the effectiveness, in this study, mastic asphalt was designed for application as the waterproofing layer on the subgrade surface of high-speed railway tracks in cold regions. The overall performance of mastic asphalt was preliminarily evaluated by laboratory tests, then a 200-m test section was constructed for field validation in northeastern China as part of a new high-speed railway line, and water content sensors were placed inside the subgrade to monitor the performance of the mastic asphalt waterproofing layer (MAWL). The subsequent field investigation and monitoring data during the two years operation showed that MAWL dramatically outperformed the conventional concrete waterproofing layer in terms of waterproof performance. Plenty of serious cracks were found in the conventional concrete waterproofing layer, but only a limited number of local cracks were observed in MAWL. As a result, MAWL keeps the water content of subgrade at a stable level. In addition, MAWL showed relatively high stability during the two years investigation period, and no obvious deterioration was observed in the test section.
The application of asphalt concrete waterproofing layer (ACWL) for the subgrade has been a trend in Chinese high-speed railway. The purpose of this research is to discuss the dynamic characteristics of full cross-section ACWL in the ballastless track structure under the train loads. The laboratory tests were conducted to evaluate the performance of the asphalt mixtures for the ACWL and a test section of ACWL was constructed on the high-speed railway in north China. The linear viscoelastic behavior of the asphalt concrete obtained from the test section was characterized by the generalized Maxwell model according to the results of dynamic modulus test. Then a 3D finite element model for the interaction system of vehicle and ballastless track structure was presented and validated by field measured data. The results indicated that the tensile strain at the bottom of the ACWL was at a relatively low level and the vertical dynamic responses of each structural layer are obviously reduced due to the application of ACWL. Therefore, the full cross-section ACWL helps to reduce the vibration of the track structure and maintain the long-term stability of the subgrade.
In this study, a new type of composite modified bitumen was developed by blending styrene-butadiene-styrene (SBS) and crumb rubber (CR) with a chemical method to satisfy the durability requirements of waterproofing material in the waterproofing layer of high-speed railway subgrade. A pressure-aging-vessel test for 20, 40 and 80 h were conducted to obtain bitumen samples in different long-term aging conditions. Multiple stress creep recovery (MSCR) tests, linear amplitude scanning tests and bending beam rheometer tests were conducted on three kinds of asphalt binders (SBS modified asphalt, CR modified asphalt and SBS/CR composite modified asphalt) after different long-term aging processes, including high temperature permanent deformation performance, resistance to low temperature thermal and fatigue crack. Meanwhile, aging sensitivities were compared by different rheological indices. Results showed that SBS/CR composite modified asphalt possessed the best properties before and after aging. The elastic property of CR in SBS/CR composite modified asphalt improved the ability to resist low temperature thermal and fatigue cracks at a range of low and middle temperatures. Simultaneously, the copolymer network of SBS and CR significantly improved the elastic response of the asphalt SBS/CR modified asphalt at a range of high temperatures. Furthermore, all test results indicated that the SBS/CR modified asphalt possesses the outstanding ability to anti-aging. SBS/CR is an ideal kind of asphalt to satisfy the demand of 60 years of service life in the subgrade of high speed railway.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.