Optical parametric chirped-pulse amplification (OPCPA) [Dubietis et al., Opt. Commun. 88, 437 (1992)] implemented by multikilojoule Nd:glass pump lasers is a promising approach to produce ultraintense pulses (>10 23 W/cm 2 ). Technologies are being developed to upgrade the OMEGA EP Laser System with the goal to pump an optical parametric amplifier line (EP OPAL) with two of the OMEGA EP beamlines. The resulting ultraintense pulses (1.5 kJ, 20 fs, 10 24 W/cm 2 ) would be used jointly with picosecond and nanosecond pulses produced by the other two beamlines. A midscale OPAL pumped by the Multi-Terawatt (MTW) laser is being constructed to produce 7.5-J, 15-fs pulses and demonstrate scalable technologies suitable for the upgrade. MTW OPAL will share a target area with the MTW laser (50 J, 1 to 100 ps), enabling several joint-shot configurations. We report on the status of the MTW OPAL system, and the technology development required for this class of all-OPCPA laser system for ultraintense pulses.
Hafnium oxide thin films with varying oxygen content were investigated with the goal of finding the optical signature of oxygen vacancies in the film structure. It was found that a reduction of oxygen content in the film leads to changes in both, structural and optical characteristics. Optical absorption spectroscopy, using nanoKelvin calorimetry, revealed an enhanced absorption in the near-ultraviolet (near-UV) and visible wavelength ranges for films with reduced oxygen content, which was attributed to mid-gap electronic states of oxygen vacancies. Absorption in the near-infrared was found to originate from structural defects other than oxygen vacancy. Luminescence generated by continuous-wave 355-nm laser excitation in e-beam films showed significant changes in the spectral profile with oxygen reduction and new band formation linked to oxygen vacancies. The luminescence from oxygen-vacancy states was found to have microsecond-scale lifetimes when compared with nanosecond-scale lifetimes of luminescence attributed to other structural film defects. Laser-damage testing using ultraviolet nanosecond and infrared femtosecond pulses showed a reduction of the damage threshold with increasing number of oxygen vacancies in hafnium oxide films.
The physical mechanisms and ensuing material modification associated with laser-induced damage in multilayer dielectric high reflectors is investigated for pulses between 0.6 and 100 ps. We explore low-loss multilayer dielectric SiO2/HfO2 mirrors which are commonly employed in petawatt-class laser systems. The spatial features of damage sites are precisely characterized, enabling the direct correlation of the observed damage morphology to the location of energy deposition and the corresponding standing-wave electric-field intensities within the layer structure. The results suggest that there are three discrete damage-initiation morphologies arising from distinctly different mechanisms: the first prevailing at laser pulse lengths shorter than about 2.3 ps, while the other two are observed for longer pulses. Modeling of the thermomechanical response of the material to localized laser-energy deposition was performed for each type of damage morphology to better understand the underlying mechanisms of energy deposition and subsequent material response.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.