The oxygen storage capacity, oxygen exchange kinetics, structure and thermodynamic stability were studied for hexagonal Y0.7Tb0.3MnO3+δ in oxygen and air to assess its applicability for oxygen separation from air by a temperature-swing adsorption process.
Single crystals of PrNiO3 were grown under an oxygen pressure of 295 bar using a unique high-pressure optical-image floating zone furnace. The crystals, with volume in excess of 1 mm3, were characterized structurally using single crystal and powder X-ray diffraction. Resistivity, specific heat, and magnetic susceptibility were measured, all of which evidenced an abrupt, first order metal-insulator transition (MIT) at ~130 K, in agreement with previous literature reports on polycrystalline specimens. Temperature-dependent single crystal diffraction was performed to investigate changes through the MIT. Our study demonstrates the opportunity space for high fugacity, reactive environments for single crystal growth specifically of perovskite nickelates but more generally to correlated electron oxides.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.