A biobased Janus molecule was used to prepare water solutions of nano-stacks made by few layer graphene.The Janus molecule was 2-(2,5-dimethyl-1H-pyrrol-1-yl)-1,3-propanediol (serinol pyrrole, SP), a serinol derivative obtained through the neat reaction of 2-amino-1,3-propandiol with 2,5-hexanedione, with atom efficiency of about 85%. SP contains the pyrrole ring, suitable for the interaction with carbon allotropes and hydroxy groups, that can easily interact with polar surroundings. Adducts, with about 14% by mass of SP, were prepared by reacting SP with a high surface area nano-sized graphite (HSAG), with about 35 graphene layers stacked in crystalline domains. Green methods were adopted, such as ball milling (HSAG-SP-M) and heating. Infrared spectra revealed peaks due to both HSAG and SP and additional peaks that could be attributed to the adduct. Both thermal and mechanical reactions left substantially unaltered the order in the graphitic layers and the interlayer distance, as shown by X-ray diffraction patterns. The relative intensity of the G and D band in the Raman spectrum was not modified by the thermal reaction, whereas enhancement of the D peak was observed after ball milling. Stable water solutions of HSAG-SP-M were prepared in a concentration range from 0.1 to 1 mg mL À1 . Centrifugation allowed isolation of adducts with few stacked graphene layers, as revealed by high resolution transmission electron microscopy. An image of the adduct showed an organic layer tightly adhered to the carbon surface. SP appears a suitable molecule for the easy functionalization of carbon allotropes, such as nanostacks of graphene layers, without substantially affecting the bulk crystalline organization and promoting the separation of the aggregates into stacks containing a low/very low number of graphene layers.

Today it is well demonstrated that stethoscopes can be as contaminated as hands, which are a recognized source of Health-Care Associated Infections (HCAIs). Ultraviolet C (UVC) light has proven disinfection capacity and the innovative UVC technology of Light Emitting Diode (LED) shows several potential benefits. To verify whether the use of UVC LEDs is effective and reliable in stethoscope membrane disinfection after prolonged use, a pre-post intervention study was conducted. A total of 1668 five-minute cycles were performed on two UVC LEDs to simulate their use; thereafter, their disinfection capacity was tested on stethoscope membranes used on a previously auscultated volunteer. Then, a further 1249 cycles were run and finally the LEDs were tested to assess performance in reducing experimental contamination by Staphylococcus aureus, Pseudomonas aeruginosa and Escherichia coli on the stethoscope membrane. Baseline volunteer contamination identified 104 Colony Forming Units (CFUs) while treated Petri dishes had 12 and 15 CFUs (p < 0.001). Statistically significant differences (p < 0.001) were also found relating to the reduction of specific bacteria: in particular, after treatment no CFU were observed for S. aureus and E. coli. UVC LEDs demonstrated the capacity to maintain high levels of disinfection after more than 240 h of use and they were effective against common microorganisms that are causative agents of HCAIs.

Electrically conductive flexible carbon papers were prepared, based on hydroxyl functionalized few layer graphene (G-OH). G-OH was obtained from the reaction of KOH with nanosized graphite with a very high surface area (HSAG), greater than 300 m2 g-1, and with high shape anisotropy, with the help of mechanical and thermal energy. Wide angle X-ray and Raman analyses showed that the core of G-OH had the structure of infinite and ideal graphene layers and that the interlayer distance between the few stacked graphene layers was the same as in pristine HSAG. Hydroxyl groups were thus essentially located in peripheral positions. High resolution transmission electron microscopy revealed the presence of graphene aggregates made by a number of layers as low as 6. Stable water suspensions were obtained, with concentrations up to 4 mg mL-1. Mild centrifugation of such suspensions had interesting efficiency as a method for producing few layer graphene: about 35% by mass of pristine HSAG was isolated as few layer graphene from supernatant suspensions. Flexible and electrically conductive carbon papers were prepared by coating a paper support with a G-OH water suspension. This work demonstrates that carbon papers can be prepared without adopting the traditional oxidation-reduction procedure, avoiding harsh reaction conditions, dangerous and toxic reagents, solvents and catalysts