Heavily Er-doped fibers (EDFs) based on P(2)O(5)-Al(2)O(3)-SiO(2) (PAS) ternary glass have been studied. A unique feature of this glass is the formation of a AlPO(4) join having a structure similar to that of SiO(2) glass and a refractive index below it. It is found that the Er(3+) absorption and emission spectra in the PAS EDFs are defined by the dopant (Al(2)O(3) or P(2)O(5)) present in excess and are close to those of the corresponding binary glass (Al(2)O(3)-SiO(2) or P(2)O(5)-SiO(2)). The presence of the AlPO(4) join results in the enhancement of the pump-to-signal conversion efficiency in the PAS EDFs as compared with the EDFs based on the P(2)O(5)-SiO(2) and Al(2)O(3)-SiO(2) (with 1.5 mol. %Al(2)O(3) and less) binary glasses. The PAS host glass is advantageous in the case of large-mode-area active fibers.
An original architecture of an active fiber allowing a nearly diffraction-limited beam to be produced is demonstrated. The active medium is a double-clad large-mode-area photonic-bandgap fiber consisting of a 10,000 ppm by weight Yb(3+)-doped core surrounded by an alternation of high- and low-index layers constituting a cylindrical photonic crystal. The periodic cladding allows the robust propagation of a approximately 200 microm(2) fundamental mode and efficiently discriminates against the high-order modes. The M(2) parameter was measured to be 1.17. A high-power cw laser was built exhibiting 80% slope efficiency above threshold. The robust propagation allows the fiber to be tightly bent. Weak incidence on the slope efficiency was observed with wounding radii as small as 6 cm.
We report, for the first time to our knowledge, on a single-mode millijoule-level 100-nanosecond Er-doped fiber laser operating near 1550 nm. The system features a newly developed 35-μm-core Yb-free double-clad Er-doped fiber based on P(2)O(5)-Al(2)O(3)-SiO(2) glass matrix and produces pulses with energy as high as 1 mJ at repetition rates of 1-10 kHz.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.