Jute fibres were subjected to a 5% alkali (NaOH) solution treatment for 0, 2, 4, 6 and 8 h at 30°C. An improvement in the crystallinity in the jute fibres increased its modulus by 12%, 68% and 79% after 4, 6 and 8 h of treatment respectively. The tenacity of the fibres improved by 46% after 6 and 8 h treatment and the % breaking strain was reduced by 23% after 8 h treatment. For the 35% composites with 4 h treated fibres, the flexural strength improved from 199⋅ ⋅1 MPa to 238⋅ ⋅9 MPa by 20%, modulus improved from 11⋅ ⋅89 GPa to 14⋅ ⋅69 GPa by 23% and laminar shear strength increased from 0⋅ ⋅238 MPa to 0⋅ ⋅2834 MPa by 19%. On plotting the different values of slopes obtained from the rates of improvement of the flexural strength and modulus, against the NaOH treatment time, two different failure modes were apparent before and after 4 h of treatment. In the first region between 0 and 4 h, fibre pull out was predominant whereas in the second region between 6 and 8 h, transverse fracture occurred with a minimum fibre pull out. This observation was well supported by the SEM investigations of the fracture surfaces.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.