X-ray luminescence and spectroscopic characteristics of Er3+ ions in a glassy lithium tetraborate matrix

Abstract

X-ray luminescence spectra of Li 2 B 4 O 7 :Er glasses have been investigated in the range of 200-800 nm. It is shown that all identified peaks in the dependence І XRL = f(λ) are due to parity-forbidden intraconfiguration radiative transitions within the 4f configuration of Er 3+ ion from excited fine-structure levels of higher lying multiplets to the ground-term level 4 I 15/2 .

Raman scattering in glassy Li2B4O7 doped with Er2O3

“…Glassy Li 2 B 4 O 7 samples were synthesized following the technology described in Refs. [22,23]. They were doped with erbium oxide Er 2 O 3 taken with the concentrations 0, 0.0005, 0.001, 0.005, 0.01 and 0.05 wt %.…”

X-ray luminescence and spectroscopic characteristics of europium ions in glassy and polycrystalline lithium tetraborate matrices

“…До складу таких боратів домішкові РЗЕ вхо-дять зазвичай як тризарядні іони, які взає-модіють із електронними і дірковими центрами захоплення розупорядкованої матриці [12,13,15]. При цьому іони РЗЕ займають у каркасі скла Li 2 B 4 O 7 взаємо-віддалені позиції і відіграють роль термо-динамічно стійких оптичних центрів, що сприяє їх власній люмінесценції [14,[16][17][18][19].…”

“…[14,16,19], досліджені енергетичні залежності суттєво відрізняються (рисунок). [17,24], або різницею типів зарядової ком-пенсації, пов'язаної зі зміною локальної симетрії, що призводить до перерозподілу інтенсивностей і збільшення неоднорід-ного уширення спектральних ліній без сут-тєвого зміщення центрів ваги окремих му-льтиплетів. Відмітимо, що для іонів групи рідких земель, внутрішні оптично активні 4f-і 5f-оболонки яких екрановані від впли-ву навколишніх іонів у матриці зовнішні-ми електронами s-, p-і d-оболонок, реалі-зується випадок слабого кристалічного поля [26].…”