Thermoplastic Polymers with Nanosilver Addition—Microstructural, Surface and Mechanical Evaluation during a 36-Month Deionized Water Incubation Period

Abstract

Three types of thermoplastic polymers, acrylonitrile butadiene styrene (ABS), polymethyl methacrylate acrylic (PMMA) and high-density polyethylene (HDPE), were enriched with silver nanoparticles (AgNPs) of 0.5 wt.% and 1.0 wt.%, respectively. The polymers and the composites were manufactured via injection molding. Regarding the potential of these polymers as matrices for long-term use as biomaterials, the aim of this study was to examine their stability in the in vitro conditions during a three-year incubation period in deionized water. In this work, microstructural observations were performed, and mechanical properties were assessed. Surface parameters, such as roughness and contact angle, were comprehensively investigated. The microstructural evaluation showed that the silver additive was homogeneously dispersed in all the examined matrices. The 36-month immersion period indicated no microstructural changes and proved the composites’ stability. The mechanical tests confirmed that the composites retained comparable mechanical properties after the silver incorporation. The Young’s modulus and tensile strength increased during long-term incubation. The addition of silver nanoparticles did not alter the composites’ roughness. The contact angle increased with the rising AgNP content. It was also shown that the materials’ roughness increased with the incubation time, especially for the ABS- and HDPE-based materials. The water environment conditions improved the wettability of the tested materials. However, the silver nanoparticles’ content resulted in the contact angle decreasing during incubation. The conducted studies confirmed that the mechanical properties of all the polymers and composites did not deteriorate; thus, the materials may be considered stable and applicable for long-term working periods in aqueous environments.

Silver-Coated Silica Nanoparticles Modified with MPS: Potential Antimicrobial Biomaterials Applied in Glaze and Soft Reliner

“…The difference among these studies has its probable cause related to the MPS utilization, since the present study employed MPS. The results of the present study agree with the findings of Ziabka et al [ 60 ], in which the contact angle had a statistically significant increase after incorporating the Ag nanoparticles.…”

Exploring the Surface Potential of Recycled Polyethylene Terephthalate Composite Supports on the Collagen Contamination Level

“…The addition of PP and HDPE components into the composite structure determined the same behaviour upon complete immersion in water since both polymers are semicrystalline with non-wettable surfaces. As expected, the low values of the swelling degree obtained after 7 days of complete immersion in water, increased in time, as an outcome of the changes in surface wettability of the polymeric materials immersed in an aqueous medium for an extended period [ 23 ].…”

Effects of graphene nanoplatelets and montmorillonite nanoclay reinforcement on dental polymethyl methacrylate

“…[ 6,7 ] Chemically modifying PMMA, inclusion of additives such as metals, fibers, and nanoparticles have been tried to achieve optimal characteristics. [ 8–12 ]…”

“…[6,7] Chemically modifying PMMA, inclusion of additives such as metals, fibers, and nanoparticles have been tried to achieve optimal characteristics. [8][9][10][11][12] Graphene nanoplatelets (GnPs) have low density, high aspect ratio, good mechanical, tribological, thermal, and electrical properties, and can be mass-produced at low costs compared to pure graphene. [13][14][15][16] GnPs have fewer defects than graphene oxides and can be effectively combined with the polymer matrix.…”