Surface photooxidation of filled polypropylene

Ryšavy̌, D.; Tkadleckova, H.

doi:10.1016/0141-3910(92)90087-l

Cited by 14 publications

(2 citation statements)

References 0 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Um aspecto importante do dióxido de titânio (tipo rutilo) é a sua capacidade de proteção à radiação ultravioleta (UV) em poliolefinas [9][10][11] . No caso do polipropileno, 2,0% de dióxido de titânio equivale à proteção oferecida por 0,2% de negro de fumo [10] , que se combinado com um estabilizante UV do tipo aminas estericamente impedidas (HALS), proporciona sinergismo bastante pronunciado na proteção à radiação ultravioleta [9 , 10] .…”

Section: Introductionunclassified

See 1 more Smart Citation

Influência de aditivos na rigidez dielétrica do polietileno de alta densidade

Ueki

Zanin

1997

Polímeros

View full text Add to dashboard Cite

Resumo: Neste trabalho são apresentados resultados de ensaios de ruptura dielétrica de curta duração com rampa de tensão positiva em amostras de polietileno de alta densidade (HDPE), modificadas com diferentes níveis de aditivos (dióxido de titânio, negro de fumo, antioxidante e estabilizante à ultravioleta). Esses resultados foram analisados estatisticamente pela distribuição de Weibull. Os parâmetros desta distribuição (β e E γ ) foram determinados pelos métodos Gráfico e de Máxima Verossimilhança. Pôde-se concluir que os aglomerados de negro de fumo são prejudiciais à rigidez dielétrica e que o parâmetro de forma β desta distribuição pode ser empregado para avaliar as condições de mistura dos componentes na formulação, as quais afetam a rigidez dielétrica. Por meio de microscopia ótica pôde-se verificar que o parâmetro β, quando determinado pelo método Gráfico, representa melhor a dispersão dos referidos aditivos na matriz polimérica. Palavras-chave: Rigidez dielétrica, polietileno de alta densidade, negro de fumo, dióxido de titânio, Weibull

show abstract

Section: Introductionunclassified

“…No caso do polipropileno, 2,0% de dióxido de titânio equivale à proteção oferecida por 0,2% de negro de fumo [10] , que se combinado com um estabilizante UV do tipo aminas estericamente impedidas (HALS), proporciona sinergismo bastante pronunciado na proteção à radiação ultravioleta [9 , 10] .…”

Section: Introductionunclassified

Influência de aditivos na rigidez dielétrica do polietileno de alta densidade

Ueki

Zanin

1997

Polímeros

View full text Add to dashboard Cite

show abstract

Photostability of isotactic polypropylene containing monoazo pigment

Ahmadi

Kish

Freeman

et al. 2008

J of Applied Polymer Sci

View full text Add to dashboard Cite

ABSTRACT:The photodegradation of isotactic polypropylene (PP) films containing a monoazo pigment and hindered amine light stabilizers (HALS) has been undertaken. PP films were exposed to medium pressure mercury lamp radiation in the laboratory for periods of up to 8 weeks and the degree of degradation (oxidation/deterioration) was examined using FTIR spectroscopy and differential scanning calorimetry (DSC) as well as by measuring changes in the mechanical properties, contact angle, and density. The results of these measurements indicate that unstabilized PP films degraded after only 240-h irradiation. By adding an organic pigment to PP films along with antioxidant and HALS, the photostability of PP films increased to the 1500-h level.

show abstract

Photodegradation of talc‐filled polypropylene

Rabello

White

1996

Polymer Composites

View full text Add to dashboard Cite

Injection‐molded talc‐filled polypropylene (PP) composites have been exposed to ultraviolet (UV) radiation in the laboratory for periods up to 26 weeks. The extent of chemical degradation has been assessed by means of Fourier transform infrared spectroscopy (FTIR) and gel permeation chromatography (GPC), and the results correlated with the mechanical properties. In the early stages of exposure, the photo‐oxidation is faster in the talc‐filled composites than in the unfilled polymer, but this trend is reversed for exposures longer than ∼12 weeks. Scanning electron microscopy (SEM) inspection has revealed that surface cracks caused by photodegradation in the filled PP occur in the surface exposed to the UV source only, resulting in much less deterioration in tensile properties when compared with the unfilled polymer which degrades significantly at the unexposed surface also. Measurements of melting temperatures by differential scanning calorimetry (DSC) gave a consistent picture of degradation with that obtained by FTIR and GPC studies. DSC analyses have also shown that an increase in the melting enthalpy for both the unfilled and filled grades occurs during exposure.

show abstract

Surface photooxidation of filled polypropylene

Cited by 14 publications

References 0 publications

Influência de aditivos na rigidez dielétrica do polietileno de alta densidade

Influência de aditivos na rigidez dielétrica do polietileno de alta densidade

Photostability of isotactic polypropylene containing monoazo pigment

Photodegradation of talc‐filled polypropylene