Influence of mechanical activation mode on morphology and phase composition of Al-2Mg-nC nanostructured composite material

Aborkin, A. V.; Evdokimov, I. A.; Vaganov, V. E.; Алымов, М. И.; Abramov, D. V.; Khorkov, K. S.

doi:10.1134/s1995078016030022

Cited by 16 publications

(3 citation statements)

References 10 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Additionally, the largest growth in the average size of the coherent scattering regions from 201 to 515 nm occurs in samples with n = 1 wt.%, while the lowest was from 107 to 162 nm with n = 9 wt.%. That is, the size of the crystallites moves from the nano-to the submicron scale, while the concentration of the nanocrystalline graphite dispersion phase has a considerable impact on the course of the regenerative processes [10].…”

Section: Resultsmentioning

confidence: 99%

FRICTION AND WEAR OF BULK NANOCOMPOSITE MATERIALS AlMg2/GRAPHITE

Aborkin

El'kin

Sobol’kov

2017

Proccedings of International Scientific Conference "BALTTRIB 2017"

View full text Add to dashboard Cite

Consolidation of nanocomposite AlMg2/graphite powders, produced by mechanical synthesis in a planetary ball mill, was carried out. Using the methods of Raman spectroscopy, and X-ray diffraction analysis, the structural-phase composition of the obtained bulk materials was studied. It was found that the samples have nanocomposite structure consisting of nanocrystalline aluminum and nanosized graphite particles. An increase in the consolidation temperature up to 450 °C leads to the formation of a dispersed phase of aluminum carbide. The effect of graphite percentage and consolidation conditions on the microhardness was estimated. Mechanisms of bulk material hardening are determined. Tribological tests of the obtained nanocomposite materials under conditions of contact interaction with 4Kh5MFS steel at a load of 1-10 N were carried out. Data on the change in the friction coefficient and magnitude of mass wear depending on the consolidation conditions and the graphite content were obtained.

show abstract

Section: Resultsmentioning

confidence: 99%

FRICTION AND WEAR OF BULK NANOCOMPOSITE MATERIALS AlMg2/GRAPHITE

Aborkin

El'kin

Sobol’kov

2017

Proccedings of International Scientific Conference "BALTTRIB 2017"

View full text Add to dashboard Cite

show abstract

“…Recently, this has become widely used mechanical processing of materials in planetary ball mills. Mechanical processing of the powder mixture is the initial stage of the technology for producing bulk composite materials and hybrid coatings [2][3][4][5][6][7][8][9].…”

Section: Introductionmentioning

confidence: 99%

Increasing of Energy-Power Indicators of Mechanical Processing in a Planetary Mill by the Use of a Working Chamber with a Square Shape of the Internal Cavity

Гусев

Sobol’kov

Aborkin

2020

SSP

View full text Add to dashboard Cite

The paper presents the results of a computational study of the influence of the geometry of the working chamber on the energy-force interaction of grinding bodies in the process of the mixture processing in a planetary mill. The method of computer simulation, using the software system, based on the ideology of discrete elements, shows the high efficiency of processing in a planetary mill, using a working chamber with a square-shaped cavity. The values of the factors that have a dominant influence on the mechanical processing of the charge are determined. A comparison with the process of processing in the working chamber of the traditional cylindrical shape is made. The research results will be used in the appointment of large-size charge processing regimes that provide a high-energy grinding process.

show abstract

“…Как показано в работах [5,6,17], молекулы фуллерена С 60 при определенных условиях формируют с атомами алюминия прочные и стабильные ковалентные связи. Кроме того, при размоле присутствие УНС способствует измельчению зерен Al, а при последующей термообработкепрепятствует протеканию процессов рекристаллизации [17,18].…”

unclassified

Nanostructured Strain-Hardened Aluminum–Magnesium Alloys Modified by C60 Fullerene Obtained by Powder Metallurgy: Part 1. The Effect of the Magnesium Concentration on the Structure and Phase Composition of Powders

Evdokimov

Khayrullin

Баграмов

et al. 2021

Russ. J. Non-ferrous Metals

Self Cite

View full text Add to dashboard Cite

Аннотация: Представлена первая часть проведенных исследований о влиянии магния на структурно-фазовый состав и физико-механические свойства наноструктурных алюминий-магниевых композиционных материалов состава Al x Mg y + + 0,3 мас.% фуллерена C 60 . Порошки композитов были получены методом совместной механоактивационной обработки исходных материалов в планетарной шаровой мельнице в среде аргона. Установлено, что они обладают сложной иерархической структурой, представляющей собой агрегаты размером 50-200 мкм, состоящие из прочных высокоплотных агломератов величиной 5-10 мкм, которые, в свою очередь, являются совокупностью наноразмерных (30-60 нм) кристаллитов. Выявлено, что увеличение концентрации магния в композите до 18 мас.% обеспечивает в процессе измельчения получение кристаллитов со средним размером менее 30 нм, при этом величина агрегатов составляет менее 50 мкм. Предельная растворимость магния в алюминии с размером кристаллитов 30-70 нм при механоактивации составила 15 мас.% (17 ат.%). Методом дифференциальной сканирующей калориметрии установлено, что при термической обработке в диапазоне температур 250-400 °С исследуемые наноструктурные композиционные материалы претерпевают необратимые структурно-фазовые превращения: рекристаллизацию, распад α-твердого раствора магния в алюминии и образование интерметаллидных β-(Al 3 Mg 2 ), γ-(Al 12 Mg 17 ) и карбидной (Al 4 C 3 ) фаз. Кроме того, на спектрах комбинационного рассеяния света присутствуют пики, соответствующие, согласно некоторым литературным источникам, ковалентным соединениям алюминия с фуллереном С 60 -алюминий-фуллереновым комплексам. На основании полученных данных в дальнейших работах будут определены параметры термобарической обработки порошковых смесей нанокомпозитов для получения объемных образцов и их испытаний.

show abstract

Influence of mechanical activation mode on morphology and phase composition of Al-2Mg-nC nanostructured composite material

Cited by 16 publications

References 10 publications

FRICTION AND WEAR OF BULK NANOCOMPOSITE MATERIALS AlMg2/GRAPHITE

FRICTION AND WEAR OF BULK NANOCOMPOSITE MATERIALS AlMg2/GRAPHITE

Increasing of Energy-Power Indicators of Mechanical Processing in a Planetary Mill by the Use of a Working Chamber with a Square Shape of the Internal Cavity

Nanostructured Strain-Hardened Aluminum–Magnesium Alloys Modified by C60 Fullerene Obtained by Powder Metallurgy: Part 1. The Effect of the Magnesium Concentration on the Structure and Phase Composition of Powders

Contact Info

Product

Resources

About