High temperature oxidation enhanced by laser remelted of CoCrFeNiAlx (x = 0.1, 0.5 and 1) high-entropy alloys

Lyu, Peng; Gao, Qi; You, Qianqian; Peng, Tao; Yuan, Haoming; Guan, Qingfeng; Cai, Jie; Liu, Haixia; Zhang, Conglin

doi:10.1016/j.jallcom.2022.165297

Cited by 14 publications

(1 citation statement)

References 27 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Oxidation parabolic rate constants (kp) were calculated from a linear fitting in the plot of (Δm/A) 2 versus t, where Δm/A represents the mass gain per unit area during the oxidation of AFA steel (in mg/cm²) and t refers to the oxidation time (in hours) [31,32].…”

Section: Oxidation Kineticsmentioning

confidence: 99%

High-temperature oxidation behavior of the as-cast and cold-rolled alumina-forming austenitic steels at 800 °C

Zhu,

Zhang,

et al. 2024

Preprint

View full text Add to dashboard Cite

The high-temperature oxidation behavior and oxidation mechanism of as-cast and cold-rolled (20%CR and 60%CR) AFA steels in dry air at 800°C were studied. The phase composition, morphology, microstructure, element distribution, and oxidation kinetics of oxidized steel were characterized and analyzed. The results show that the mass gains of both as-cast and cold-rolled samples increase rapidly within the first 100 h. During the subsequent long-term high-temperature oxidation process, the mass gains of as-cast and 60%CR samples slowly increase, while the mass gain of 20%CR AFA steel fluctuates greatly. The oxide layer comprises an outer oxide layer rich in (Fe,Cr) oxide and an inner oxide layer rich in Al2O3. The reduction in the oxidation resistance of AFA steel under small deformation is because defects such as dislocations introduced by deformation provide more channels for the diffusion of atoms, while the reason for the improvement under large deformation is that more δ-ferrite and precipitated B2-NiAl phase can promote the rapid formation of Al2O3 film and reduce further oxidation of the matrix. However, because of the formation of aluminum oxide film on the surface of the samples, both as-cast and cold-rolled AFA steels exhibit complete oxidation resistance at 800°C.

show abstract

Section: Oxidation Kineticsmentioning

confidence: 99%