Evaluation of resin adhesion to zirconia ceramic using some organosilanes

Matinlinna, Jukka Pekka; Heikkinen, Timo; Özcan, Mutlu; Lassila, Lippo; Vallittu, Pekka K.

doi:10.1016/j.dental.2005.11.035

Cited by 176 publications

(180 citation statements)

References 18 publications

Supporting

Mentioning

169

Contrasting

Unclassified

Order By: Relevance

“…A previous study reports that the silica content on the silica-coated surface is about 11%, and these particles do not appear to have become embedded on the zirconia surface. 29 Therefore, the G1 failure mode may have been influenced, leading to the similar bond strengths, in comparison with the other experimental groups. In addition, the limitations of the μsbs test, such as non-uniform stress distribution, must be considered, because this distribution may influence the failure mode.…”

Section: Discussionmentioning

confidence: 99%

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment

et al. 2015

View full text Add to dashboard Cite

This study evaluated the influence of an alternative surface treatment on the microshear bond strength (μsbs) of zirconia-based ceramic. Thirty-five zirconia disks were assigned to five groups according to the following treatments: Control (CO), glass and silane were not applied to the zirconia surface; G1, air blasted with 100μm glass beads + glaze + silane; G2, a gel containing 15% (by weight) glass beads applied to the ceramic surface + glaze + silane; G3, a gel containing 25% (by weight) glass beads applied to the ceramic surface + glaze + silane; and G4, a gel containing 50% (by weight) glass beads applied to the ceramic surface + glaze + silane. The specimens were built up using RelyX ARC ® , according to the manufacturer's recommendations, and inserted in an elastomeric mold with an inner diameter of 0.8 mm. The μsbs test was performed using a testing machine at a crosshead speed of 0.5 mm/min. ANOVA and Tukey's test (p < 0.05) were applied to the bond strength values (in MPa). CO (15.6 ± 4.1) showed the lowest μsbs value. There were no statistical differences between the G1 (24.9 ± 7.4), G2 (24.9 ± 2.3), G3 (35.0 ± 10.3) and G4 (35.3 ± 6.0) experimental groups. Those groups submitted to surface treatments with higher concentrations of glass showed a lower frequency of adhesive failures. In conclusion, the glass application improved the interaction between the ceramic and the luting cement.

show abstract

Section: Discussionmentioning

confidence: 99%

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment

et al. 2015

View full text Add to dashboard Cite

show abstract

“…Thus, several surface conditioning methods have been suggested to condition zirconia surfaces physically and/or chemically where physico-chemical conditioning methods remain to be the best methods to increase adhesion of resin-based materials to zirconia [2][3][4][5][6][7][8][9][10].…”

Section: Introductionmentioning

confidence: 99%

Could readily silanized silica particles substitute silica coating and silanization in conditioning zirconium dioxide for resin adhesion?

Özcan

Yetkiner

2015

Journal of Adhesion Science and Technology

Self Cite

View full text Add to dashboard Cite

Particle deposition with silica-coated alumina followed by silane application increase the physico-chemical interaction between the resin cement and zirconia.Unfortunately, due to hydrolytic degradation of the silane, achieved adhesion decreases after aging conditions. Recently, readily silanized silica particles became available, that eliminates silanization procedures. This study investigated the effect of particle types with different morphology and surface properties on the surface wettability and adhesion of resin cement to zirconia after aging. Zirconia specimens (5x5x1 mm 3 ) (Emax ZirCAD, Ivoclar)were wet polished to 1200 grit silicone carbide abrasive and ultrasonically cleaned.Specimens were randomly assigned to one of the following surface conditioning protocols Failure types were exclusively adhesive in all groups. Weibull distribution presented lower 3 shape ( 0 ) for AL (7.7) and SIL (5.3) and the highest for SILP (10.8). Silane coated silica particles (SilJet Plus) presented better wettability on zirconia than with alumina or alumina particles coated with silica and provided similar bond strength on zirconia obtained with silica coated and silanized surfaces. Since no silane application is needed with readily silanized silica particles, it may be used as a substitute for conventional silica coating and silanization, reducing the clinical procedures.

show abstract

“…Bunun nedeni de silan ajanı uygulayabilmek için zirkonya seramik yüzeyine uygulanan silika tabakasının yüzeye çok sıkı bağlanmaması ve zamanla zirkonya seramik yüzeyinden ayrılmasıdır. 20 Suni yaşlandırma aşamasında test öncesinde genellikle suda bekletme, termal döngü ve mekanik yükleme uygulanmaktadır. 21,22 Çalışmamızda da suni yaşlandırma aşamasında örneklere termal döngü uygulanmıştır.…”

Section: Discussionunclassified

Effect of surface conditioning on bond strength between zirconia ceramic and composite resin luting agent

Toman¹,

Toksavul²,

Gökçe³

et al. 2014

EÜ Dişhek Fak Derg

View full text Add to dashboard Cite

ÖzetAMAÇ: Zirkonya seramik restorasyonların adeziv simantasyonu için seramik yüzeyini hazırlama yöntemlerinin kompozit rezin siman ile zirkonya seramik ara yüzeyindeki bağlanma direnci üzerine etkilerini incelemek ve bağlanma direnci açısından etkili olan en iyi yöntemi belirlemektir. YÖNTEMLER: Bu çalışmada, her bir grupta 60 adet örnek olacak şekilde toplam 6 adet grup oluşturuldu. Oluşturulan 6 grup, kullanılan 2 farklı yapıştırma sistemine bağlı olarak 2 alt gruba ayrıldı. Daha sonra alt gruplar da termal döngü uygulanıp uygulanmamasına göre 2'şer alt gruba daha ayrıldı. Böylece her bir yüzey hazırlama sistemi için toplam 4 adet alt grup oluşturuldu. 360 adet 3 mm çapında ve 4 mm yüksekliğinde kompozit örnek hazırlandı. Simantasyon aşamasında toplam 6 farklı yüzey hazırlama işlemi (Yüzey işlemi yok, Kumlama, Kumlama+Ceramic Primer, Kumlama+Metal/Zirconia Primer, CoJet, Rocatec) uygulandı ve her bir yüzey hazırlama işlemi için 2 farklı kompozit rezin siman (Panavia F ve Multilink Automix) ve her bir siman için termal döngü uygulanıp uygulanmamasına göre 2 alt gruba daha ayrıldı. Kesme deneyi Universal test cihazında 0.5 mm/dak hızda yapıldı. Elde edilen verilerin istatistiksel analizinde üç yönlü varyans analizi yapıldı (p<0.05). Zirkonya seramik yüzeyini hazırlama yöntemlerini tek tek karşılaştırmak için Tukey testi uygulandı (p<0.05). BULGULAR: En yüksek bağlanma direnci değeri 18.25 MPa ile kumlama sonrası Ceramic Primer ajanın uygulandığı Multilink ile simante edilen ve termal döngü uygulanmayan örneklerde elde edildi. İstatistiksel olarak en düşük bağlanma direnci değeri hiçbir yüzey hazırlama işleminin uygulanmayıp Multilink ile simante edilen ve termal döngü uygulanan örneklerde elde edildi (p<0.05). SONUÇ: Çalışmanın bulgularına göre zirkonya seramik kullanılarak hazırlanan restorasyonların kompozit rezin siman zirkonya seramik ara yüzeyindeki bağlanma direnci açısından uygulanabilecek en iyi yöntemler kumlama işlemi sonrası Ceramic Primer ya da Zirconia Primer ajan uygulamaktır. Anahtar Kelimeler: bağlanma direnci, zirkonya seramik, adeziv simantasyon

show abstract

Evaluation of resin adhesion to zirconia ceramic using some organosilanes

Cited by 176 publications

References 18 publications

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment

Could readily silanized silica particles substitute silica coating and silanization in conditioning zirconium dioxide for resin adhesion?

Effect of surface conditioning on bond strength between zirconia ceramic and composite resin luting agent