Análise microestrutural, tenacidade à fratura e vida em fadiga das AA7050-T7451 e AA2050-T84 (Al-Li)

Fatigue crack propagation of aeronautic AA7050-T7451 and AA2050-T84 aluminum alloys in air and saline environments

“…On the other hand, L-T orientation presents a "barrier effect" at grain boundaries, promoting a slight decrease in FCGR. This decrease in FCGR can be due to the clustering of second phase particles in the rolling direction, raising the proportion of intergranular failures in T-L oriented specimens, thus reducing fracture toughness [26], [27]. The saline environment has amplified the FCGR in the AA7050-T7451 alloy and had a minor effect on the AA2050-T84 alloy (see Figure 3b).…”

Estudo de fadiga e tenacidade de ligas de alumínio e alumínio-lítio soldadas por fricção-mistura (FSW) submetidas a atmosferas corrosivas e criogênicas

“…Micrografia de microscopia eletrônica de transmissão (MET) da liga 2050-T84 mostrando, em sinal de campo claro, precipitados finos dentro dos grãos, e precipitados grosseiros nos contornos de grãos, e os respectivos mapeamentos elementares de raios-X através de EDX. (b) Al, (c) Mn, (d) Mg, (e) Cu e (d) Zn [12]. …”