A comparative study on the flux pinning properties of Zr-doped YBCO film with those of Sn-doped one prepared by metal-organic deposition

Abstract

We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped YBa 2 Cu 3 O 7-δ (YBCO) films with the same thickness of ~350 nm for a comparative purpose. The films were prepared on the SrTiO 3 (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density (J c) and pinning force density (F p). The anisotropic J c,min /J c,max ratio in the field-angle dependence of J c at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic J c values of 9.0 and 2.9 MA/cm 2 with the maximum F p (F p,max) values of 19 and 5 GN/m 3 at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller BaZrO 3 (BZO) nanoparticles (the average size ≈ 28.4 nm) than YBa 2 SnO 5.5 (YBSO) nanoparticles (the average size ≈ 45.0 nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.