Correlação entre grau de conversão, microdureza e conteúdo inorgânico em compósitos

Abstract

The purpose of this study was to evaluate the correlation between degree of conversion and microhardness in dental composites, as well as the effect of the inorganic content and type of photo-curing unit on these parameters. Three indirect composites (Artglass, Solidex and Zeta LC) were polymerized by means of three different laboratorial units (UniXS, Solidilite and an experimental device). For each material, fifteen samples were prepared using a metal matrix. The degree of conversion was analyzed by means of infrared spectroscopy, and microhardness was also assessed. The inorganic content was measured by means of thermogravimetric analysis (TGA). The Pearson s test was carried out in order to determine correlations. The degree of conversion of Artglass ranged from 37.5% to 79.2%, and its microhardness, from 32.4 to 50.3 (r = 0.904). The degree of conversion of Solidex ranged from 41.2% to 60.4%, and its microhardness, from 33.3 to 44.1 (r = 0.707). The degree of conversion and the microhardness of Zeta LC ranged from 62.0% to 78.0% and from 22.6 to 33.6, respectively (r = 0.710). It was concluded that the utilization of different photo-curing units caused variations on the degree of conversion, as a result of specific characteristics of each unit. For each material, there was strong correlation between the degree of conversion and microhardness. In addition, when different materials were compared, microhardness was more affected by filler content than by the degree of conversion.

Avaliação do grau de conversão de resinas compostas fotoativadas em diferentes tempos e potências

“…Associadas a esse fator, avaliações clínicas e laboratoriais sugerem que há associação entre o grau de conversão e as propriedades físico-mecânicas, tais como estabilidade de cor, resistência ao desgaste, à flexão ou à tração das resinas 6 . A densidade de potência emitida pelas fontes de luz deve ser no mínimo de 300 mW/cm 2 a 400 mW/cm 2 para polimerizar adequadamente um incremento de 1,5 mm a 2 mm de resina composta 1,7 .…”

“…O percentual de duplas ligações de carbono alifáticas não convertidas (% C=C) é determinado pela taxa da intensidade de absorção entre ligações C=C (1.638 cm -1 ) e ligações C=O (1.730 cm -1 ), antes e após a polimerização. O grau de conversão correspondente é calculado pela subtração dessa taxa de 100% 6 .…”

Effect of different post-cure polymerization treatment on composite resin hardness

“…The degree of conversion varies according to the composition of the materials, including monomeric systems, initiator and solvent concentration, amount and type of particles [8][9][10] .…”

"Estudo do efeito da distância da ponta de aparelhos fotoativadores na microdureza e no grau de conversão da resina composta usando luz halógena, laser de argônio e LED"

“…BRYANT, 1990;CALDAS et al, 2003;MANGA;CHARLTON;WAKEFIELD, 1995;CHUNG;GREENER, 1990;CONSANI et al, 2002;CORRER-SOBRINHO et al, 2000;VOUGIOUKLASKIS;CAPUTO, 1987;ERSOY et al, 2004;FERRACANE, 1985;FERRACANE;GREENER, 1986;HANSEN;ASMUSSEN, 1997;KANCA 3rd , 1985;KNOBLOCH et al, 2004;MANDARINO et al, 1992;MASUDA;MALUF;MUENCH, 1999;MARTINS et al, 2002;NAUFEL;NEVES et al, 2002;PERIS et al, 2005;PILO;CARDASH, 1992;PIRES et al, 1993;ANDREOU, 2004;RAMOS;GARONE NETTO;BURGER, 2003;RODE et al, 2001;RODE et al, 2005;RYGE;FOLEY;FAIRHURST, 1961;SANTOS, 2003;SAY et al, 2003;UMBEHAUN, 2001;COMBE, 1987 …”

“…Apesar de alguns estudos não terem encontrado correlação entre a dureza e o grau de conversão (CHUNG e GREENER, 1990;VOUGIOUKLASKIS;CAPUTO, 1987). Ferracane (1985), Ferracane e Greener (1986), Neves et al (2002) e Santos (2003, mostraram haver essa correlação. A diferença nesses resultados pode ser explicada pelo fato de que, segundo Ferracane (1985) essa correlação existe quando é comparada resina composta da mesma composição e nos trabalhos onde não foi encontrada a correlação foram comparadas resinas diferentes.…”