Swine deep bedding ashes as a mineral additive for cement based mortar

Abstract

The sustainability of intensive swine production demands alternative destinations for the generated residues. Ashes from swine rice husk-based deep bedding were tested as a mineral addition for cement mortars. The ashes were obtained at 400 to 600ºC, ground and sieved through a 325 mesh sieve (# 0.045 mm). The characterization of the ashes included the determination of the index of pozzolanic activity with lime. The ashes were also tested as partial substitutes of Portland cement. The mortars were prepared using a cement:sand proportion of 1:1.5, and with water/cement ratio of 0.4. Three percentages of mass substitution of the cement were tested: 10, 20 and 30%. Mortar performances were assessed at 7 and 28 days determining their compressive strength. The chosen condition for calcinations at the laboratory scale was related to the maximum temperature of 600ºC since the resulting ashes contained vitreous materials and presented satisfactory values for the pozzolanic index under analysis. The pozzolanic activity indicated promising results for ashes produced at 600ºC as a replacement of up to 30% in cement masses. Key words: rice husk, pozzolanicity, vitreous silica, sustainability CINZAS DE CAMA SOBREPOSTA DE SUÍNOS COMO ADIÇÃO MINERAL EM ARGAMASSAS DE CIMENTORESUMO: A sustentabilidade das regiões de produção intensiva de suínos requer destinos alternativos para os resíduos gerados. Cinzas de cama sobreposta de suínos à base casca de arroz, foram testadas como adição mineral em substituição ao cimento. As cinzas foram obtidas nas temperaturas de 400 a 600ºC, moídas e passadas por peneira ABNT 325 (# 0,045 mm). A caracterização de cinzas incluiu a determinação do índice de atividade pozolânica com a cal. As cinzas também foram testadas como substitutos parciais de cimento Portland. As argamassas foram preparadas na proporção cimento:areia de 1:1,5 e com fator água-cimento de 0,4. Três porcentagens de substituição do cimento comercial foram usadas: 10, 20 e 30% em massa. O desempenho das argamassas foi avaliado aos 7 e aos 28 dias com a determinação da resistência à compressão axial. A condição escolhida para calcinações em escala laboratorial foi associada à temperatura máxima de 600ºC, uma vez que as cinzas resultantes continham material vítreo e apresentavam valores satisfatórios para o índice de pozolanicidade em análise. A atividade pozolânica indicou resultados promissores para as cinzas produzidas a 600ºC e com substituição de até 30% em massa de cimento. Palavras-chave: casca de arroz, pozolanicidade, sílica vítrea, sustentabilidade

Transformação Da Casca De Arroz Em Um Produto De Maior Valor Agregado: Potencial Para a Produção De Painéis Particulados

“…Silica occurs in the cell walls in virtually all aerial parts of rice plant, and is most abundant in the husk (PARK et al, 2003). Ashes from calcination of rice husk deep bedding contain about 42% of silica oxide (DI CAMPOS et al, 2008). The presence of higher concentrations of this component and waxes in rice husk than those of wood may hide reactive sites for adhesion with polar adhesives, affecting panel bond resistance (NDAZI et al, 2007;PARK et al, 2003).…”

Aplicação da cinza da casca do arroz em argamassas de assentamento

“…Os resíduos vegetais como a cinza da casca do arroz (CCA), vêm sendo estudados por vários pesquisadores (Bui et al, 2005;Della et al, 2005;Agarwal, 2006;Nair et al, 2006;Di Campos et al, 2008;Ganesan et al, 2008;Menezes et al, 2008;Kieling et al, 2009;Ramezanianpour et al, 2009;Rashid et al, 2010;Zerbino et al, 2011) os quais observaram que esta cinza apresenta bons resultados em diversas aplicações, como por exemplo, quando utilizada em argamassas e concretos.…”

Aproveitamento das cinzas da queima da cama sobreposta de suínos para substituição parcial do cimento Portland.

“…A Tabela 3 apresenta a composição química de três tipos de CCA, com a variação da taxa de aquecimento e a existência ou não de tratamento químico. A sustentabilidade na produção animal vem sendo cada dia mais estudada (MATTHEWS, 1996;GUIVANT, 1996;ROELER;CESCONETO, 2001;PANDORFI, 2002;DI CAMPOS et al, 2005). Apesar de altamente tecnificada e com alta produção, a criação intensiva de suínos apresenta alguns aspectos problemáticos relacionados ao bem-estar animal, ao alto custo inicial de instalação e à grande quantidade de dejetos orgânicos produzidos (CORRÊA, 1998;PANDORFI, 2005 Pra OLIVEIRA et al (2005), a produção de suínos em sistema de cama sobreposta, nas fases de creche e terminação, constitui-se uma alternativa viável para a produção de suínos em substituição ao sistema de criação sobre piso ripado (total ou parcial).…”