Hidrólise de celulose por catalisadores mesoestruturados NiO-MCM-41 e MoO3-MCM-41

Textural properties of nickel, palladium and titanium oxides supported on MCM-41 materials and their application on oxidative desulfurization of dibenzothiophene

“…The titanium oxide showed peaks with 2θ = 25.5°, 38.1°, 48.1° and 54.5° which are characteristic of anatase titanium IV oxide 5 ( Figure 1d). Similar results were also previously found in other works when the nickel or palladium was supported on siliceous materials 12,13 . FTIR spectra for MCM-41 calcinated and non-calcinated samples are shown in Figure 2.…”

“…The presence of nickel, palladium or titanium oxides phases along with the MCM-41 materials were observed in the prepared samples. Peaks corresponding to NiO phase 12 was confirmed by the low intensity peaks at 2θ = 37.1° and 43.2° (Figure 1b). Also PdO phase was identified by peaks at 2θ = 33.6°, 41.7° and 54.4° (Figure 1c).…”

“…All materials show bands at 1240 cm -1 and 800 cm -1 which are assigned to symmetric and asymmetric stretching of the Si-O-Si bond, which are very common in silicates. Further, the materials shown an absorption band in the range of 1550 to 1750 cm -1 attributed to water interacting with the support surface (Figure 3a) showed mass loss in the range 30-600 °C, which is due to both the desorption of adsorbed water molecules, as well as, the loss of silanol groups existing on the calcinated material [11][12][13][14] . Samples of MCM-41 impregnated with precursors of nickel (Figure 3b), palladium (Figure 3c) or titanium (Figure 3d) presented respective mass loss in the temperature range of 30 to 900 °C, data shown in detail in Table 1.…”

Hidrogenação Do Breu Utilizando Catalisador De Paládio Suportado Em Carvão Ativo

“…Observa-se uma predominância de mesoporos (20 -500 Å) em relação aos microporos (20 Å) e macroporos (> 500 Å). O uso de catalisadores mesoporosos é mais vantajoso no que se refere ao acesso dos substratos reacionais aos sítios ativos do catalisador (SILVA et al, 2012).…”

Síntese do material mesoporoso MCM-41 usando esponja de água-doce como fonte de sílica

“…1 Esses materiais foram descobertos no início da década de 90 pelos pesquisadores da Mobil, obtendo uma nova família de materiais mesoporosos com tamanho de poros bem definidos e ajustáveis, com grandes áreas específicas, da ordem de 1000 m 2 g -1 , a qual foi denominada M41S. 2,3 MCM-41 se destaca como um dos membros mais importantes desta família, exibindo um arranjo hexagonal de mesoporos unidimensionais o qual permite o acesso a moléculas grandes, tais como, polietilenoglicol (PEG), 4 celulose, 5 triacilglicerídeos, 6 ácidos graxos 7 e ácido fosfotúngstico. 8 Ademais, possui excelente estabilidade térmica, além da vasta aplicação catalítica em um número maior de substratos do que as zeólitas comuns.…”