Morfologia e cristalinidade de hidroxicarbonato de zinco obtido via precipitação homogênea: influência dos ânions cloreto e nitrato

Abstract

IONS. The effects of chloride and nitrate anions and their respective concentrations, as well as urea presence, on solid phase morphologies were investigated. Zinc hydroxide carbonate was prepared by aging diluted zinc salt solution in presence of urea at 90 o C. Samples were identified by X-ray powder diffractograms showing the characteristic patterns of hydrozincite. The crystallinity was correlated with the concentrations of reagents. Spherulitic-type aggregates and single acicular particles were obtained from diluted chloride and nitrate solutions while porous aggregates of uniform size were formed from solutions with high chloride and urea concentrations.Keywords: zinc hydroxide carbonate; homogeneous precipitation; morphology; spherulites. ARTIGO INTRODUÇÃONas últimas décadas pesquisadores em todo o mundo buscam incessantemente métodos viáveis e reprodutíveis para a preparação de dispersões coloidais com controle morfológi-co [1][2][3] . A princípio tais pesquisas foram fundamentadas principalmente na utilização dessas dispersões para avaliação de modelos teóricos, os quais propõem algumas características físicas de materiais. Compostos monodispersos são de grande aplicabilidade em alta tecnologia, e têm despertado interesses não somente quanto à composição química, mas também na correlação existente entre as propriedades físicas, forma e tamanho de partícula [3][4][5] . O controle da forma e do tamanho de partícula é de grande importância, principalmente na produção de materiais catalíticos, luminescentes, varistores, pigmentos e no processamento de filmes finos 1-7. . Diversos métodos vem sendo utilizados para a obtenção de dispersões coloidais, objetivando um melhor controle de forma e de distribuição de tamanho de partícula. Os principais méto-dos de preparação podem ser resumidamente divididos em três classes 1 : (i) precipitação homogênea, (ii) transformação de fases e (iii) reações com aerossóis. O método mais utilizado é a precipitação homogênea o qual consiste em atingir a supersaturação crítica das espécies que formam a fase sólida, tal que, a formação de núcleos se faça por um processo extremamente rápido e único. O desenvolvimento destes núcleos ocorre posteriormente ao processo de nucleação resultando assim, em dispersões com estreita distribuição de tamanho e com homogeneidade de forma 1,3 . Óxido de zinco possui diversas aplicações tecnológicas tais como: catalisadores, aditivos em óleos lubrificantes, varistores, materiais luminescentes, sensores de gás, entre outras. Industrialmente é obtido principalmente pela oxidação dos vapores de zinco, produzindo partículas de diversas formas . O controle da forma das partículas de óxido de zinco pode ser realizado através da precipitação homogênea do hidroxicarbonato de zinco (hidrozincita), que termodecomposto, produz óxido de zinco com manutenção da forma das partículas 2,8,9 . Composição, tamanho e forma de partícula são fortemente dependentes de um grande número de fatores experimentais, tais como: concentração de reagentes, pH, temperatura, e n...

Toxicological effects of pure and amine-functionalized ZnO nanorods on Daphnia magna and Lactuca sativa

“…At 1575 cm −1 , according to the literature, this band is attributed to the carbonyl of the acetate, and at around 1400 cm −1 , there are bands characteristic of aliphatic C-H. 57 At approximately 500 cm −1 , binding bands of Zn-O could be observed. 58 The main absorption bands that characterize the amine-functionalization of ZnO NRs appear at 2927 cm −1 and 2854 cm −1 , assigned to asymmetric and symmetric stretching vibrations of aliphatic C-H, respectively. Also, the region of 3400 cm −1 indicates the overlap of hydroxyl group bands with the amine.…”

A influência do tipo de ânion sobre a sinterabilidade e as características elétricas de cerâmicas varistoras obtidas a partir de soluções coloidais

“…As misturas de pós cerâmicos foram preparadas, a partir dos reagentes acima considerados e de forma a se obter a composição química final em base calcinada supracitada, tendo-se em vista os estudos desenvolvidos por Duarte [15] e Ferreira [16] acerca da influência das técnicas de preparação sobre o desempenho de cerâmicas varistoras. Para tanto, em cada caso, preparou-se os respectivos sistemas coloidais constituídos pelos reagentes de interesse (usando-se, separadamente, os precursores do óxido de zinco) e obteve-se os pós cerâmicos através da técnica de precipitação homogênea via termólise da uréia, em sistema reacional com temperatura controlada [11,15]. Conforme o reagente precursor do óxido de zinco utilizado denominou-se os sistemas cerâmicos produzidos da seguinte forma: Sistema I (obtido a partir do acetato de zinco), Sistema II (obtido a partir do cloreto de zinco) e Sistema III (obtido a partir do nitrato de zinco).…”

“…Em geral, a pesquisa em métodos químicos de síntese e preparação de pós cerâmicos visa não apenas a produção de pós de alta pureza e composição química controlada, mas também ao controle de tamanho e forma de partícula, os quais têm se tornado cada vez mais importantes em função da crescente demanda por artefatos e dispositivos cerâmicos de alto desempenho [4,[11][12][13][14]. No caso dos varistores, a utilização de controles e de rotas químicas para produção e mistura de pós cerâmicos utilizados na manufatura destes dispositivos, podem resultar em vantagens em relação aos métodos convencionais de mistura de pós, pois têm potencial para proporcionar um melhor controle da distribuição do tamanho das partículas, do grau de aglomeração e da pureza do pó produzido.…”

Propriedades ópticas e estruturais de óxido de zinco contendo enxofre

“…et al 25 (2003), Özgur,U et al 26 Dentre os principais métodos de preparação do óxido de zinco, a síntese hidrotérmica 18 é o que possui maior destaque. Porém diversos outros métodos são utilizados, como a síntese em meio homogêneo 21 , o método Pechini 19 , e a decomposição térmica de sulfeto de zinco, que foi o método empregado neste trabalho com base em resultados anteriormente obtidos pelo grupo de pesquisa 30 .…”