Calcium
silicate minerals can react with CO2 to form
calcium carbonate and have been proposed to be a sustainable binder
as a potential CO2 sinker. In this study, the carbonation
characteristics are comparatively assessed among calcium silicates
having different calcium/silica (Ca/Si) ratios and polymorphs (CS,
C3S2, γ-C2S, β-C2S, C3S). Calcium silicate compacts exposed to a
100% CO2 environment at a 0.4 MPa pressure were tested
for carbonation temperature evolution, degree of carbonation (DOC),
mechanical properties, and microstructural characterization. Results
indicate γ-C2S is the most reactive, reaching a DOC
of 50% in 24 h, followed by C3S2, CS, β-C2S, and C3S, which generally agrees with the pattern
of the cumulative normalized temperature increase. Meanwhile, carbonated
β-C2S compact attains the highest compressive strength
of 80 MPa in 24 h, followed by γ-C2S, C3S2, and C3S, while CS only reaches 20 MPa.
Calcite and aragonite are the preferable polymorphs of calcium carbonate
in the carbonated C3S, γ-C2S, β-C2S, and C3S2, while only the carbonation
of CS generates vaterite in addition to calcite and aragonite. The
unreacted grains coated by a thin rim of calcium-modified silica gels
are encapsulated by the continuous calcium carbonates, which composes
the skeleton of the carbonated calcium silicates.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.