A new class of multifunctional polymers based on poly(l,6heptadiyne) derivatives with various functional groups such as carbazole unit for photoconductive polymers and nonlinear optical (NLO) chromophores for NLO polymers were synthesized by metathesis polymerization. The polymerizations were carried out with MoCI,-and WCI,-based catalysts. The catalytic activity of MoCI, was found to be greater than that of WCI , . The resulting polymers exhibited photoconductivity and large optical nonlinearity. These conjugated polymers have good solubility in common organic solvents, long-term stability toward air oxidation, and high electrical conductivity.

No abstract

No abstract

A new series of high brightness and luminance efficient poly(p-phenylenevinylene) (PPV)-based electroluminescent (EL) polymers, poly[2-[4-[5-(4-(3,7-dimethyloctyloxy)phenyl)-1,3,4-oxadiazole-2-yl]phenyloxy]-1,4-phenylenevinylene] (Oxa-PPV), poly[2-[2-((3,7-dimethyloctyl)oxy)phenoxy]-1,4-phenylenevinylene] (DMOP-PPV), and their corresponding random copolymers, poly[[2-[4-[5-(4-(3,7-dimethyloctyloxy)phenyl)-1,3,4-oxadiazole-2-yl]phenyloxy]-1,4-phenylenevinylene]-co-[2-[2-((3,7-dimethyloctyl)oxy) phenoxy]-1,4-phenylenevinylene]] (Oxa-PPV-co-DMOP-PPV), with an electron-deficient 1,3,4-oxadiazole unit on the side groups, were synthesized through the Gilch polymerization method. The newly designed and synthesized asymmetric molecular structures of Oxa-PPV, DMOP-PPV, and Oxa-PPV-co-DMOP-PPV were completely soluble in common organic solvents, and defect-free optical thin film was easily spin-coated onto the indium tin oxide (ITO) substrate. Oxa-PPV shows a high glass transition temperature (T(g)), which might be an advantage for long time operation of polymer light-emitting diodes (PLEDs). Double-layer LEDs with an ITO/PEDOT/polymer/Al configuration were fabricated by using those polymers. Electrooptical properties and device performance could be adjusted by introducing the Oxa-PPV content in the copolymers. The emission colors could be tuned from green to yellowish-orange via intramolecular energy transfer. The improved device performance of Oxa-PPV over DMOP-PPV and Oxa-PPV-co-DMOP-PPV may be due to better electron injection and charge balance between holes and electrons and also efficient intramolecular energy transfer from 1,3,4-oxadiazole units to PPV backbones. The maximum brightness and the luminance efficiency of Oxa-PPV were up to 19395 cd/m(2) at 14 V and 21.1 cd/A at 5930 cd/m(2). The maximum luminance efficiency of Oxa-PPV is ranked the highest value among the PPV derivatives to date.