Theoretical and experimental results have revealed that the lithium-ion storage capacity for nitrogen-doped graphene largely depends on the nitrogen-doping level. However, most nitrogen-doped carbon materials used for lithium-ion batteries are reported to have a nitrogen content of approximately 10 wt% because a higher number of nitrogen atoms in the two-dimensional honeycomb lattice can result in structural instability. Here we report nitrogen-doped graphene particle analogues with a nitrogen content of up to 17.72 wt% that are prepared by the pyrolysis of a nitrogen-containing zeolitic imidazolate framework at 800°C under a nitrogen atmosphere. As an anode material for lithium-ion batteries, these particles retain a capacity of 2,132 mA h g À 1 after 50 cycles at a current density of 100 mA g À 1 , and 785 mAh g À 1 after 1,000 cycles at 5 A g À 1 . The remarkable performance results from the graphene analogous particles doped with nitrogen within the hexagonal lattice and edges.

The scalable production of hydrogen could conveniently be realized by alkaline water electrolysis. Currently, the major challenge confronting hydrogen evolution reaction (HER) is lacking inexpensive alternatives to platinum-based electrocatalysts. Here we report a high-efficient and stable electrocatalyst composed of ruthenium and cobalt bimetallic nanoalloy encapsulated in nitrogen-doped graphene layers. The catalysts display remarkable performance with low overpotentials of only 28 and 218 mV at 10 and 100 mA cm−2, respectively, and excellent stability of 10,000 cycles. Ruthenium is the cheapest platinum-group metal and its amount in the catalyst is only 3.58 wt.%, showing the catalyst high activity at a very competitive price. Density functional theory calculations reveal that the introduction of ruthenium atoms into cobalt core can improve the efficiency of electron transfer from alloy core to graphene shell, beneficial for enhancing carbon–hydrogen bond, thereby lowing ΔGH* of HER.

An FeCo alloy covered with nitrogen doped graphene is prepared by direct annealing of Fe3[Co(CN)6]2nanoparticles, exhibiting efficient HER catalysis.