Constructing multifunctional electromagnetic interference (EMI) shielding films with superior mechanical strength has sparked a lot of interest in the fields of wearable electronics. In this work, the conductive silver nanowires (AgNWs) were synthesized and impregnated into the highly aligned cellulose scaffold (CS) fabricated by wood delignification followed by hot-pressing and polydimethylsiloxane (PDMS) dipping processes to obtain the outstanding EMI shielding cellulosic film (d-AgNWs@CS-PDMS). The consecutively conductive pathway of AgNWs was constructed in the microchannels of the CS as a result of the hydrogen bonding between AgNWs and cellulose fibers, which is conducive to the reflection of incident EM waves. The higher degree of nanofiber alignment and the compact conductive network were improved by densification upon hot pressing, which endows the composite film with striking mechanical properties (maximum tensile strength of 511.8 MPa) and superb EMI shielding performance (shielding effectiveness value of 46 dB with a filler content of 21.6 wt %) at the X band (8.2–12.4 GHz). Moreover, the existence of an intensive AgNWs network and the introduction of the PDMS layer improve the hydrophobicity and antibacterial activity of the composite film, avoiding serious health concerns in the long-term wearing. These results demonstrate that the obtained d-AgNWs@CS-PDMS composite film has high potential as an EMI shielding material used for wearable devices.

An optical transparent and hazy film with admirable flexibility, electromagnetic interference (EMI) shielding, and Joule heating performance meeting the requirements of optoelectronic devices is significantly desirable. Herein, a cellulose paper was infiltrated by epoxy resin to fabricate a transparent cellulose paper (TCP) with high transparency, optical haze, and favorable flexibility, owing to effective light scattering and mechanical enhancement of the cellulose network. Moreover, a highly connected silver nanowire (AgNW) network was constructed on the TCP substrate by the spray-coating method and appropriate thermal annealing technique to realize high electrical conductivity and favorable optical transmittance of the composite film at the same time, followed by coating of a polydimethylsiloxane (PDMS) layer for protection of the AgNW network. The obtained PDMS/AgNWs/TCP composite film features considerable optical transmittance (up to 86.8%) and haze (up to 97.7%), while satisfactory EMI shielding effectiveness (SE) (up to 39.1 dB, 8.2–12.4 GHz) as well as strong mechanical strength (higher than 41 MPa) were achieved. The coated PDMS layer prevented the AgNW network from falling off and ensured the long-term stability of the PDMS/AgNWs/TCP composite film under deformations. In addition, the multifunctional PDMS/AgNWs/TCP composite film also exhibited excellent Joule heating performance with low supplied voltages, rapid response, and sufficient stability. This work demonstrates a novel pathway to improve the performance of multifunctional transparent composite films for future advanced optoelectronic devices.

No abstract