A strictly anaerobic thiosulfate-reducing bacterium was isolated from a corroding offshore oil well in Congo and was designated strain SEBR 4207T. Pure culture of the strain induced a very active pitting corrosion of mild steel, with penetration rates of up to 4 mm per year. This constitutes the first experimental evidence of the involvement of thiosulfate reduction in microbial corrosion of steel. Strain SEBR 4207T cells were vibrios (3 to 5 by 1 pm), stained gram negative, and possessed lateral flagella. Spores were not detected. Optimum growth occurred in the presence of 3% NaCl at pH 7.0 and 42°C. Strain SEBR 4207T utilized peptides and amino acids, but not sugars or fatty acids. It fermented serine, histidine, and Casamino Acids, whereas arginine, glutamate, leucine, isoleucine, alanine, valine, methionine, and asparagine were only used in the presence of thiosulfate. Peptides were fermented to acetate, isobutyrate, isovalerate, 2-methylbutyrate, H,, and CO,. The addition of either thiosulfate or sulfur but not sulfate increased peptide utilization, growth rate, and biomass; during growth, H,S was produced and a concomitant decrease in H, was observed. The addition of either thiosulfate or sulfur also reversed H, inhibition. 16s rRNA sequence analysis indicates that strain SEBR 4207T is distantly related to members of the genus Thermoanuerobacter (83% similarity). Because the phenotypic and phylogenetic characteristics cannot be assigned to any described genus, strain SEBR 4207T is designated as a new species of a new genus, Dethiosulfovibrio peptidovorans gen. nov., sp. nov. Strain SEBR 4207T has been deposited in the Deutsche Sammlung von Mikroorganismen und zellkulturen GmbH (= DSM 11002).In 1989, Elf Congo experienced corrosion of the first 5 km of a 23-km main subsea pipeline that transported sour oil (i.e., H,S-containing petroleum) produced from the Emeraude oil field. The corroded segment was replaced, but it corroded again a year later. The whole line was then replaced and operated under a specifically designed biocide treatment regimen. The preliminary examination of the corroded iron showed that the breakthrough was due to bacterial pitting corrosion, with an unusually high penetration rate of about 1 cm per year. Chemical analysis of the pipeline water revealed the presence of up to 0.5 mM thiosulfate. It is likely that the thiosulfate was produced as a result of oxidation of the H,S naturally present in the oil field ecosystem by oxygen that is introduced in the pipelines during processing (10, 15, 22). The corrosion of pipelines was suspected to be due not only to sulfate but also to thiosulfate reduction by sulfate-reducing bacteria (SRB), because computer modeling had shown that thiosulfate reduction could induce the pitting corrosion of steel at higher rates than sulfate reduction (13).Since the pipeline was under a biocide treatment regimen during our microbiological investigations, the production fluids from several wellheads upstream of the line were collected and analyzed. Besides diffe...

No abstract

No abstract

Microbes recovered from sediments, slime, tubercles, or corrosion coupons were characterized into functional groups, identified by fatty acid patterns and used in a flow-through test system. Test solutions were prepared as field conditions and supplemented with nutrients for the growth of microbes. Four-sided working electrodes were fabricated to simplify experimental design by combining four steel disks from the same stock into one probe. Concentric electrodes were made to simulate localized corrosion and study the effect of bacteria upon stability of localized corrosion. Electrochemical techniques such as: open circuit potential, electrochemical impedance spectroscopy, and galvanic current measurements were performed to evaluate the corrosion of mild steel in solutions containing different combinations of bacteria. Actual microbial community on the electrode surface was recovered by culture methods for viable counts upon termination of experiments. Preliminary results indicated that this test system provided an accelerated testing to simulate field exposures.

No abstract