Magnetic Fe3O4@poly(m-phenylenediamine) particles (Fe3O4@PmPDs) with well-defined core-shell structure were first designed for high performance Cr(VI) removal by taking advantages of the easy separation property of magnetic nanoparticles (MNPs) and the satisfactory adsorption property of polymers. Through controlling the polymerization on MNPs, directly coating was realized without the complicated premodification procedures. The particle property and adsorption mechanism were analyzed in details. Fe3O4@PmPDs exhibited tunable PmPD shell thickness from 10 to 100 nm, high magnetic (∼150 to ∼73 emu g(-1)) and facile separation property by magnet. The coating of PmPD significantly enhanced Cr(VI) adsorption capacity from 46.79 (bare MNPs) to 246.09 mg g(-1) (71.55% PmPD loading proportion), much higher than many reported composite adsorbents. The high Cr(VI) removal performance was attributed to the adsorption of Cr(VI) on protonated imino groups and the efficient reduction of Cr(VI) to Cr(III) by amine, followed by Cr(III) chelated on imino groups, which are spontaneous and endothermic. The Fe3O4@PmPDs have great potential in treating Cr(VI)-contaminated water.

No abstract

Hierarchical porous Fe3O4 particles with tunable grain size were synthesized based on a facile poly (diallyldimethylammonium chloride) (PDDA)-modulated solvothermal method. The products were characterized with scanning electron microscopy (SEM) and transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), N2 adsorption-desorption technique, vibrating sample magnetometer (VSM), and dynamic light scattering (DLS). The results show that increasing the PDDA dosage decrease the grain size and particle size, which increased the particle porosity and enhanced the surface area from 7.05 to 32.75 m(2) g(-1). Possible mechanism can be ascribed to the PDDA function on capping the crystal surface and promoting the viscosity of reaction medium to mediate the growth and assembly of grain. Furthermore, the arsenic adsorption application of the as-obtained Fe3O4 samples was investigated and the adsorption mechanism was proposed. High magnetic Fe3O4 particles with increased surface area display improved arsenic adsorption performance, superior efficiency in low-level arsenic removal, high desorption efficiency, and satisfactory magnetic recyclability, which are very promising compared with commercial Fe3O4 particles.