We report here a systematic investigation of the mechanical properties of polylactic acid (PLA) processed by fused filament fabrication (FFF) 3D printing vs PLA processed by compression molding. Our results show that the tensile strength and modulus of FFF‐PLA is 49% and 41% lower, respectively, than compression molded samples of PLA. We also demonstrate here an approach to augment the mechanical properties of 3D printed PLA using nanocellulose. Incorporation of a small quantity (1 wt%) of cellulose nanofibers (CNF) was found to enhance the tensile strength and modulus of 3D printed PLA by 84% and 63%, respectively. X‐ray microtomography was used to probe the morphology of 3D printed PLA and PLA/CNF composites. 3D printed PLA/CNF composites had significantly lesser voids as compared to neat 3D printed PLA. Differential scanning calorimetry study revealed that CNF can accelerate the nucleation and crystallization of 3D printed PLA leading to enhanced crystallinity. The thermal stability of 3D printed PLA/CNF composites was not compromised by the addition of CNF. The enhanced mechanical properties of 3D printed PLA/CNF composites can be ascribed to higher crystallinity and lesser defects.

No abstract

Waste leather buff (WLB) filled polycaprolactone (PCL) composites were prepared by twin‐screw extrusion varying the WLB content from 2% to 40%. These composites were extensively characterized by several techniques in order to establish micro and macroscopic properties. Addition of WLB resulted in improvement of tensile modulus of neat PCL and reduction in percentage crystallinity of PCL matrix was observed with increase in WLB content. Interfacial adhesion and dispersion of WLB on PCL matrix was investigated using Scanning Electron Microscope. Percentage of water uptake increased with increase in concentration of WLB in the composite. These biodegradable composites could be used to develop low cost materials suitable for applications in footwear industry, for making bags, suitcases, etc., eliminating the environmental issues arising from WLB generated from tanneries in leather industry. POLYM. COMPOS., 38:2889–2897, 2017. © 2015 Society of Plastics Engineers

We report here enhanced ferroelectric crystal formation and energy generation properties of polyvinylidene fluoride (PVDF) in the presence of surface-modified crystalline nanocellulose. Incorporation of only 2−5 wt % fluorinated nanocellulose (FNC) in PVDF has been found to significantly induce polar β/γ-phase crystallization as compared to the addition of unmodified nanocellulose (carboxylated nanocellulose). A device made up of electrically poled PVDF/FNC composite films yielded 2 orders of magnitude higher voltage output than neat PVDF in vibrational energy harvesting. This remarkable increase in energy generation properties of PVDF at such a low loading of an organic natural biopolymer could be attributed to the tailored surface chemistry of nanocellulose, facilitating strong interfacial interactions between PVDF and FNC. Interestingly, energy harvesting devices fabricated from PVDF/FNC nanocomposites charged a 4.7 μF capacitor at significantly faster rate and the accumulated voltage on capacitor was 3.8 times greater than neat PVDF. The fact that PVDF/FNC nanocomposites still retain a strain at break of 10− 15% and can charge a capacitor in few seconds suggests potential use of these nanocomposites as flexible energy harvesting materials at large strain conditions.