Poly(N‐isopropylacrylamide) (NIPAAm) is well known as a smart material with good thermal sensitivity and favorable biocompatibility. A series of new smart hydrogels, NIPAAm copolymerized with IAM (itaconamic acid; 4‐amino‐2‐methylene‐4‐oxobutanoic acid), were synthesized through radical solution polymerization in this work. Poly(NIPAAm‐co‐IAM) can respond to the changes of temperature as well as pH value. Such a characteristic is due to the fact that IAM contains not only a hydrophilic acrylic acid moiety but also an acrylamide moiety to be thermal and pH sensitive. The experimental results show that the lower critical solution temperature (LCST) of the copolymer increases as the molar fraction of IAM increases. Moreover, based on the current experimental data, 3 wt % of Poly(NIPAAm‐co‐IAM) aqueous solution in this study exhibits a phase transition temperature (37.8°C) close to the human body temperature in the buffer solution of pH 7 possibly to be useful in drug delivery. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 42367.

A series of semi-interpenetrating polymer network (semi-IPN) hydrogels were synthesized and investigated in this study. Linear copolymer poly(N-isopropylacrylamide-co-itaconamic acid) p(NIPAM-co-IAM), which is formed by copolymerization of N-isopropylacrylamide (NIPAM) and itaconamic acid (IAM, 4-amino-2-ethylene-4-oxobutanoic acid), was introduced into a solution of NIPAM to form a series of pH and thermo dual-responsive p(NIPAM-co-IAM)/pNIPAM semi-IPN hydrogels by free radical polymerization. The structural, morphological, chemical, and physical properties of the linear copolymer and semi-IPN hydrogels were investigated. The semi-IPN hydrogel showed high thermal stability according to thermal gravimetric analyzer (TGA). Scanning electronic microscopy (SEM) images showed that the pore size was in the range of 119~297 µm and could be controlled by the addition ratio of the linear copolymer in the semi-IPN structure. The addition of linear copolymer increased the fracture strain from 57.5 ± 2.9% to 91.1 ± 4.9% depending on the added amount, while the compressive modulus decreased as the addition increased. Moreover, the pH and thermo dual-responsive properties were investigated using differential scanning calorimetry (DSC) and monitoring the swelling behavior of the hydrogels. In deionized (DI) water, the equilibrium swelling ratio of the hydrogels decreased as the temperature increased from 20 °C to 50 °C, while it varied in various pH buffer solutions. In addition, the swelling and deswelling rates of the hydrogels also significantly increased. The results indicate that the novel pH-thermo dual-responsive semi-IPN hydrogels were synthesized successfully and may be a potential material for biomedical, drug delivery, or absorption application.

No abstract