The microstructures and passivation behavior of selective laser melted 316L stainless steel (SLM SS316L) after various heat treatments (500 °C, 950 °C, and 1100 °C) were investigated. The electrochemical results showed that the SLM SS316L sample that was heat treated at 950 °C exhibited the lowest passive current density. The microstructural characterization analysis indicated that the subgrain structures transformed from dislocation-rich subgrain boundaries into island-like cellular trace structures after heat treatment at 950 °C. This led to improved corrosion resistance due to the elimination of dislocations and the homogenization of the composition. Compositional analyses of the passive film indicated that there was no notable change in the passive film composition after heat treatment at 500 °C and 950 °C. However, heat treatment at 1100 °C promoted the formation of Cr(OH)3 in the passive film, resulting in a reduced corrosion resistance. Based on these results, heat treatment at 950 °C appears to be an adequate post-process for SLM SS316L to optimize the microstructure, while also improving corrosion resistance.
The hydrogen permeation behaviour of X80 pipeline steel exposed to corrosion environments with different H 2 S/CO 2 partial pressure ratios at room temperature was investigated through the highpressure electrochemical hydrogen permeation test. Both CO 2 and H 2 S have a hydrogen permeation promoting effect; however, CO 2 hydrogen permeation promoting effect is much weaker than H 2 S. The hydrogen permeation curves have the rising, falling then stable stage. When at a total pressure of 1 MPa, as the H 2 S partial pressure decreases, the hydrogen permeation promoting effect weakens, but the peak current of hydrogen permeation gradually increases. The main reason is that the role of corrosion products has changed from promoting hydrogen permeation to hindering hydrogen permeation during the reaction.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.