Focused ion beam (FIB) milling is a versatile maskless and resistless patterning technique and has been widely used for the fabrication of inverse plasmonic structures such as nanoholes and nanoslits for various applications. However, due to its subtractive milling nature, it is an impractical method to fabricate isolated plasmonic nanoparticles and assemblies which are more commonly adopted in applications. In this work, we propose and demonstrate an approach to reliably and rapidly define plasmonic nanoparticles and their assemblies using FIB milling via a simple "sketch and peel" strategy. Systematic experimental investigations and mechanism studies reveal that the high reliability of this fabrication approach is enabled by a conformally formed sidewall coating due to the ion-milling-induced redeposition. Particularly, we demonstrated that this strategy is also applicable to the state-of-the-art helium ion beam milling technology, with which high-fidelity plasmonic dimers with tiny gaps could be directly and rapidly prototyped. Because the proposed approach enables rapid and reliable patterning of arbitrary plasmonic nanostructures that are not feasible to fabricate via conventional FIB milling process, our work provides the FIB milling technology an additional nanopatterning capability and thus could greatly increase its popularity for utilization in fundamental research and device prototyping.

A simply and reproducible way is proposed to significantly suppress the nucleation density of graphene on the copper foil during the chemical vapor deposition process. By inserting a copper foil into a tube with one close end, the nucleation density on the copper foils can be reduced by more than five orders of magnitude and an ultra-low nucleation density of ~10 nucleus/cm2 has been achieved. The structural analyses demonstrate that single crystal monolayer graphene with a lateral size of 1.9 mm can be grown on the copper foils under the optimized growth condition. The electrical transport studies show that the mobility of such single crystal graphene is around 2400 cm2/Vs.

Third-order optical nonlinearities of graphene from monolayer to multilayers were investigated in the femtosecond regime, and the contribution of interlayer coupling to the nonlinearities was studied. The nonlinear refractive index γ of the order of 10−9 cm2/W and the nonlinear absorption coefficient β of 10−6 cm/W were obtained. By systematically investigating the nonlinear optical properties with the number of layers and comparing the coupling graphene with the decoupling superimposed graphene, we found that the coupling of interlayers has large effect upon the nonlinear refraction. These results provide an effective approach for developing graphene-based nonlinear photonic devices

No abstract