Purpose
This paper aims to optimize the erosion wear analysis of slurry impeller material. Stainless steel (SS-410) was used as the pump impeller material. This erosion test was established to influence the rotational speed, solid concentration, time period and particle size. Fly ash was used as the erodent material.
Design/methodology/approach
The erosion wear experiments were performed at different particle size, rotational speed, time duration and solid concentration (by weight). These tests were performed at four different speeds of 750, 1,000, 1,250 and 1,500 rpm, and the time durations of these experiments are 75, 120,165 and 210 min. For protective coating, high-velocity oxygen-fuel spray process was used for depositing WC-10Co-4Cr coating on stainless steel. To investigate the influence of controlled process parameters on slurry erosion wear of pump impeller material, Taguchi method was used.
Findings
Results show that significant improvement in erosion wear resistance has been observed by using WC-10Co-4Cr coating. The process parameters affecting the erosion wear loss were in following order: time > rpm > concentration > particle size. The means of signal-to-noise ratio of stainless steel SS410 with and without coating vary from 93.56 to 54.02 and from 86.02 to 48.18, respectively.
Originality/value
For the erosion wear rate of both uncoated and coated stainless steel, the most powerful influencing factor was identified as time. The erosion test reveals that the coating exhibits ductile erosion mechanism and shows better erosion wear resistance (approximately two times) compared to uncoated stainless steel.
The fracture properties of cortical bone are directly coupled to its complex hierarchical structure. The limited availability of bone material from many anatomic locations creates challenges for assessing the effect of bone heterogeneity and anisotropy on fracture properties. The small punch technique was employed to examine the fracture behavior of cortical bone in terms of area under the curve values obtained from load–load point displacement behavior. Fracture toughness of cortical bone was also determined in terms of J-toughness values obtained using a compact tension (CT) test. Area under the curve values obtained from the small punch test were correlated with the J-toughness values of cortical bone. The effects of bone density and compositional parameters on area under the curve and Jtoughness values were also analyzed using linear and multiple regression analysis. Area under the curve and J-toughness values are strongly and positively correlated. Bone density and %mineral content are positively correlated with both area under the curve and J-toughness values. The multiple regression analysis outcomes support these results. Overall, the findings support the hypothesis that area under the curve values obtained from small punch tests can be used to assess the fracture behavior of cortical bone.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.