The aim of this study was to compare intrapulpal temperature increase produced by high-speed handpiece, Er:YAG laser and CVDentus ultrasound tips during cavity preparation. Thirty bovine mandibular incisors with an enamel/dentin thickness of 4 mm at buccal surface had their roots amputated and were allocated to the following groups (n=10): Group I- high-speed handpiece; Group II- noncontact Er:YAG laser (250 mJ/4Hz); and Group III- CVDentus ultrasouns tips. All devices were used with water cooling. Class V cavities were prepared to a depth of 3.5 mm, measured with a periodontal probe. A type T thermocouple was placed inside the pulp chamber to determine the temperature increase (°C), which was recorded by a data acquisition system ADS 2000 IP (Lynx Technology) linked to a notebook computer. Data were analyzed statistically by oneway ANOVA and Tukey's test (p=0.05). The mean temperature rises were: 1.10°C (±0.56) for Group I, 0.84°C (±0.55) for Group II, and 3.00°C (± 1.34) for Group III. There were no statistically significant differences (p>0.05) between Groups I and II, but both of them differed significantly from Group III (p<0.05). In conclusion, the use of Er:YAG laser and high-speed handpiece for cavity preparation resulted in similar temperature increase. Although ultrasound tips generated significantly higher intrapulpal temperature increase, it remained below the critical value of 5.5°C and may be considered safe for use.

This study evaluated the effects of excess cement removal techniques, with or without subsequent polishing, on biofilm formation and micromorphology in the marginal region of the tooth/restoration. From bovine teeth, 96 dentin blocks (4 × 8 × 2 mm) were produced, molded, and reproduced in type IV gypsum, on which 96 pressed ceramic blocks (Vita PM9, Vita Zahnfabrik; 4 × 8 × 2 mm) were produced via the lost wax technique. The dentin blocks and their respective ceramic blocks were cemented with a self-adhesive resin cement (RelyX U200, 3M ESPE), and cement excess was removed from the margin using four different techniques, followed or not by polishing with silicone rubber tips: MBr, removal with microbrush and photoactivation; MBr-Pol, MBr + polishing; Br, removal with brush and photoactivation; Br-Pol, Br + polishing; Photo-Expl, 5 seconds of initial photoactivation, removal with explorer, and final curing; Photo-Expl-Pol, Photo-Expl + polishing; Photo-SB, 5 seconds of initial photoactivation, removal with scalpel, and final curing; and Photo-SB-Pol, Photo-SB + polishing. After 24 hours, the roughness in the marginal region was analyzed using a profilometer (three measurements on each sample). Micromorphological analyses of the region were performed by stereomicroscope and scanning electron microscopy (SEM). Then the samples were contaminated with sucrose broth standardized suspension with Streptococcus mutans , Staphylococcus aureus , and Candida albicans and incubated for a period of 48 hours. The samples were quantitatively analyzed for bacterial adherence in the marginal region by confocal laser scanning microscopy and counting of colony-forming units (CFUs/mL) and qualitatively analyzed using SEM. Roughness data (Ra) were submitted to two-way analysis of variance, Tukey test at a confidence level of 95%, and Student t-tests. CFU, biomass, and biothickness data were analyzed by Kruskal-Wallis, Mann-Whitney, and Dunn tests. The removing technique statistically influenced Ra (MBr, p=0.0019; Br, p=0.002; Photo-Expl, p=0.0262; Photo-SB, p=0.0196) when comparing the polished and unpolished groups. The MBr and MBr-Pol technique differed significantly for CFU/mL values (p=0.010). There was no significant difference in the amounts of biomass and biothickness comparing polished and unpolished groups and when all groups were compared (p>0.05). Different morphological patterns were observed (more regular surface for polished groups). We conclude that margin polishing after cementation of feldspar/pressed ceramic restorations is decisive for achieving smoother surfaces, as the excess cement around the edges can increase the surface roughness in these areas, influencing bacterial adhesion.

Objective:The purpose of this study was to compare the accuracy of two working cast fabrication techniques using strain- gauge analysis.Methods:Two working cast fabrication methods were evaluated. Based on a master model, 20 working casts were fabricated by means of an indirect impression technique using polyether after splinting the square transfer copings with acrylic resin. Specimens were assigned to 2 groups (n=10): Group A (GA): type IV dental stone was poured around the abutment analogs in the conventional way; Group B (GB), the dental stone was poured in two stages. Spacers were used over the abutment analogs (rubber tubes) and type IV dental stone was poured around the abutment analogs in the conventional way. After the stone had hardened completely, the spacers were removed and more stone was inserted in the spaces created. Six strain-gauges (Excel Ltd.), positioned in a cast bar, which was dimensionally accurate (perfect fit) to the master model, recorded the microstrains generated by each specimen. Data were analyzed statistically by the variance analysis (ANOVA) and Tukey's test (α= 5%).Results:The microstrain values (με) were (mean±SD): GA: 263.7±109.07με, and GB: 193.73±78.83με.Conclusion:There was no statistical difference between the two methods studied.

Objective:This study evaluated the influence of porcelain (VM9, VITA Zahnfabrik, Germany) thickness on the flexural strength and crack propagation in bilayered zirconia systems (YZ, VITA Zahnfabrik, Germany).Material and Methods:Thirty zirconia bars (20.0x4.0x1.0 mm) and six zirconia blocks (12.0x7.5x1.2 mm) were prepared and veneered with porcelain with different thickness: 1 mm, 2 mm, or 3 mm. The bars of each experimental group (n=10) were subjected to four-point flexural strength testing. In each ceramic block, a Vickers indentation was created under a load of 10 kgf for 10 seconds, for the propagation of cracks.Results:The results of flexural strength were evaluated by One-way ANOVA and Tukey's test, with a significance level of 5%. The factor “thickness of the porcelain” was statistically significant (p=0.001) and the l-mm group presented the highest values of flexural strength. The cracks were predominant among the bending specimens with 1 and 2 mm of porcelain, and catastrophic failures were found in 50% of 3-mm-thick porcelain. After the indentation of blocks, the most severe defects were observed in blocks with 3-mm-thick porcelain.Conclusion:The smallest (1 mm) thickness of porcelain on the zirconia infrastructure presented higher values of flexural strength. Better resistance to defect propagation was observed near the porcelain/ zirconia interface for all groups. Higher flexural strength was found for a thinner porcelain layer in a bilayered zirconia system. The damage caused by a Vickers indentation near and far the interface with the zirconia shows that the stress profiles are different.

No abstract