In this study, we investigated the influence of light intensity on the surface-free energy and dentin bond strength of single-step selfetch adhesives. The adhesives were applied to the dentin surfaces of bovine mandibular incisors and cured with light intensities of 0 (no irradiation), 200, 400, and 600 mW/cm 2 . Surface-free energies were determined by measuring the contact angles of three test liquids placed on the cured adhesives. Dentin bond strengths of the specimens were also measured. Polymerization with a higher light intensity resulted in a lower surface-free energy of the cured adhesives. The greatest bond strength was achieved when a light intensity of 400 mW/cm 2 or greater was used. Our data suggest that the surface-free energy and dentin bond strength of single-step self-etch adhesives are affected by light intensity of the curing unit.
The influence of methyl mercaptan on the repair bond strength of composites fabricated using self-etch adhesives was investigated. The surface free-energies were determined by measuring the contact angles of test liquids placed on composites that had been immersed in different concentrations of methyl mercaptan (0.01, 0.1, and 1.0 M). To determine the repair bond strength, self-etch adhesives were applied to the aged composite, and then newly added composites were condensed. Ten samples of each specimen were subjected to shear testing at a crosshead speed of 1.0 mm min(-1). Samples were analyzed using two-way ANOVA followed by Tukey's honestly significant difference (HSD) test. Although the dispersion force of the composites remained relatively constant, their polar force increased slightly as the concentration of methyl mercaptan increased. The hydrogen-bonding forces were significantly higher after immersion in 1.0 M methyl mercaptan, leading to higher surface-free energies. However, the repair bond strengths for the repair restorations prepared from composites immersed in 1.0 M methyl mercaptan were significantly lower than for those immersed in 0.01 and 0.10 M methyl mercaptan. Considering the results of this study, it can be concluded that the repair bond strengths of both the aged and newly added composites were affected by immersion in methyl mercaptan solutions.
We compared the surface free energies and dentin bond strengths of two-step self-etch systems with and without an oxygen-inhibited layer. The adhesives were applied to self-etching primer-treated dentin surfaces of bovine incisors, after which the teeth were light-irradiated and the oxygen-inhibited layer was left intact or removed with ethanol. We determined surface free energies (γ S ) and their components by measuring the contact angles of three test liquids placed on the cured adhesives. We also measured the dentin bond strengths of chemically cured resin composite to the adhesives, with and without the oxygen-inhibited layer. For all surfaces, the estimated surface tension component,
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.