Among the recently discovered Fe-based superconducting compounds, the (K,Ba)Fe2As2 phase is attracting large interest within the scientific community interested in conductor developments. In fact, after some years of development, critical current densities Jc of about 10 5 A/cm 2 at fields up to more than 10 T have been obtained in powder in tube (PIT) processed wires and tapes. Here we explore the crucial points in the wire/tape fabrication by means of the exsitu PIT method. We focus on scaling up processes which are crucial for the industrial fabrication. We analyzed the effects on the microstructure of the different heat and mechanical treatments. By an extensive microstructural analysis correlated with the transport properties we addressed the issues concerning the phase purity, the internal porosity and crack formation in the superconducting core region. Our best conductors with a filling factor of about 30 % heat treated at 800 °C exhibited Tc = 38 K the highest value measured in such kind of superconducting tape. The microstructure analysis shows clean and well connected grain boundaries but rather poor density: The measured Jc of about 3•10 4 A/cm 2 in self-field is suppressed by less than a factor 7 at 7 T.Such not yet optimized Jc values can be accounted for by the reduced density while the moderate in-field suppression and a rather high n-factor confirm the high homogeneity and uniformity of these tapes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.