GdVO 4 nanoparticles doped with Dy3+ have been prepared using urea hydrolysis method in ethylene glycol medium. Linear decrease in the unit cell volume indicates the quantitative substitution of Gd3+ lattice sites by Dy3+ in GdVO4. The luminescence intensity of electric dipole transition at 573 nm is more than that of magnetic dipole transition at 483 nm. This has been attributed to the asymmetric environment of Dy3+ ion in GdVO4. Luminescence intensity decreases with increasing Dy3+ concentrations due to concentration quenching. This is supported by lifetime decay studies. There is no particle size effect on the peak positions of Dy3+ emission. There is an increase in the decay lifetime for F49/2 level with increase in heat treatment from 500 to 900 °C. This is attributed to the reduction in nonradiative process arose from surface inhomogeneities. The decay lifetime data follow the biexponential to monoexponential nature with increase of Dy3+ concentrations. There is an increase in the quantum yield with the increase in heat treatment temperature.
Nanoparticles of GdVO4 doped with Eu3+ and core/shell of GdVO4:Eu3+/GdVO4 are prepared by urea hydrolysis method using ethylene glycol as capping agent as well as reaction medium at 130 °C. Unit cell volume increases when GdVO4 is doped with Eu3+ indicating the substitution of Gd3+ lattice sites by Eu3+. From luminescence study, it is confirmed that there is no particle size effect on emission positions of Eu3+. Optimum luminescence intensity is found to be in 5–10 at. % Eu3+. Above these concentrations, luminescence intensity decreases due to concentration quenching effect. There is an enhancement in luminescence intensity of core/shell nanoparticles. This has been attributed to the reduction in surface inhomogenities of Eu3+ surroundings by bonding to GdVO4 shell. The lifetime for D50 level increases with annealing and core/shell formation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations –citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.