The novelty of this study consists in the formulation and characterization of three experimental dental composites (PM, P14M, P2S) for cervical dental lesion restoration compared to the commercial composites Enamel plus HRi® - En (Micerium S.p.A, Avengo, Ge, Italy), G-ænial Anterior® - Ge, (GC Europe N.V., Leuven, Belgium), Charisma® - Ch (Heraeus Kulzer, Berkshire, UK). The physio-chemical properties were studied, like the degree of conversion and the residual monomers in cured samples using FTIR-ATR (attenuated total reflectance) and HPLC-UV (ultraviolet detection), as well as the evaluation of the mechanical properties of the materials. The null hypothesis was that there would be no differences between experimental and commercial resin composites regarding the evaluated parameters. Statistical analysis revealed that water and saliva storage induced significant modifications of all mechanical parameters after three months for all tested materials, except for a few comparisons for each type of material. Storage medium seemed not to alter the values of mechanical parameters in comparison with the initial ones for: diametral tensile strength (DTS-saliva for Ge and PM, compressive strength (CS)-water for Ch, DTS-water and Young’s modulus YM-saliva for P14M and YM-water/ saliva for P2S (p > 0.05). Two of the experimental materials showed less than 1% residual monomers, which sustains good polymerization efficiency. Experimental resin composites have good mechanical properties, which makes them recommendable for the successful use in load-bearing surfaces of posterior teeth.

No abstract

No abstract

BackgroundThe use of electronic media has been found to be a risk factor for higher BMI and for being overweight. Physical activity has been found to be associated with lower BMI and lower risk for being overweight. Little is known about whether the associations between physical activity and electronic media use are additive or interactive in predicting BMI and risk for overweight among adolescents.MethodsThe data used in this study stem from the 2009/2010 survey of “Health Behaviour in School-aged Children (HBSC) study: A WHO Cross-National Survey. The sample consisted of 107184 13 and 15 year students from 30 different countries. Multilevel regression models were used to produce the presented estimates.ResultsOverall, 18% of boys and 11% of girls were classified as overweight. EM use was found to be associated with increased BMI z-scores and odds for overweight among both boys and girls who did not comply with physical activity guidelines. Among physically active adolescents, EM was found to be significantly associated with BMI or odds for overweight among girls, but not among boys.ConclusionWhile the usage of EM appear to be inconsequential for BMI and the risk of overweight among physically active boys, we find evidence indicating that EM use is associated with BMI and risk for overweight among girls, including those who report complying with MVPA guidelines.

Restoration of noncarious cervical lesions with resin composites is one of the treatment options, but the retention of the restorations located at the crown-root junction is still a cause of clinical concern. The aim of this study was to evaluate the adhesive properties of three experimental resin composites and two commercial materials used to restore cavities prepared on extracted teeth as well as to determine the relative elemental composition of these materials. We tested the null hypothesis, which considered that the adhesive behaviours of different resin composites did not differ. The microleakage test using tracers showed that all tested materials exhibited some degree of dentinal microleakage, although they all had good dentinal adhesion. The results failed to reject the null hypothesis. The scanning electron microscopy revealed completely adapted adhesive interfaces underneath the restorations along with well-developed hybrid layers depending on the adhesive system. Energy dispersive X-ray analysis analyses showed that the restorative materials have similar chemical compositions, with some differences between the samples from the same material. The results support the implementation of experimental resins in clinical settings.