The optical qualities of cutting-edge aesthetic dental ceramics are crucial for great aesthetics and may be impacted by various bleaching methods. The objectives of this study were to evaluate how home bleaching affected the translucency parameter (TP), contrast ratio (CR), total color difference (ΔE), and surface roughness (Ra) of various aesthetic dental ceramics, including innovative ultra-translucent zirconia. The three varieties of ceramics that were tested—IPS e.max-Press (IPS); classic zirconia with feldspathic layering (LZr); and translucent zirconia (TZr)—were each represented by seven samples. The samples were bleached at home using 15% carbamide peroxide for six hours a day for seven days. Each specimen’s pre- and post-bleaching CIE L*a*b* values were measured using a spectrophotometer, and the TP, CR, and ΔE were determined. Ra values were measured via 3D profilometry. In comparison to the pre-stage results, statistical analysis showed a significant decrease in TP and increase in CR for LZr and TZr in the post-stage (p < 0.05), but not for IPS (p = 0.398). The results also showed substantial variations in ΔE for the three ceramics (p = 0.020). Ra readings during the post-stage were noticeably greater than those at the pre-stage (p = 0.018). Home bleaching had an impact on the optical characteristics and surface texture of the dental ceramics. Additionally, IPS had greater color stability than LZr and TZr.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.